热处理对定向凝固Co基合金微观组织的影响
Alternative TitleEffect of Heat-treatment on Microstructure of Directional Solidification Co-base Superalloy
孙跃军; 林陌思; 葛艳辉; 张军
Source Publication热加工工艺
2011
Volume40Issue:12Pages:152-154,159
ISSN1001-3814
Abstract利用XRD和扫描电镜研究了热处理对一种定向凝固Co基合金微观组织的影响。结果表明:Co基合金的铸态组织主要由Co的固溶体基体、M_7C_3、MC和M_(23)C_6碳化物组成,其中M_7C_3和MC为块状,主要分布在枝晶间,M_(23)C_6呈颗粒状,分布在块状M_7C_3和MC周围。合金经1150℃×4h固溶处理后,大部分块状M_7C_3和MC溶入Co的固溶体基体中,在随后的空冷中析出颗粒状M_(23)C_6。在870℃和970℃时效时,随时效温度的升高和时效时间的延长,合金中M23C6的尺寸逐渐增大。
Other AbstractThe effects of heat-treatment on the microstructure of directional solidification Co-base superalloy were investigated using XRD and SEM.The results show that the microstructure of Co-base superalloy as-cast is composed of Co matrix,M7C3,MC and M23C6.Among them,MC and M7C3 distributes in inter dentrite and M23C6 near the MC and M7C3.After solid solution heat-treating at 1150 ℃ for 4 h,most MC and M7C3 dissolves into Co-base matrix,M23C6 is deposited from Co matrix during following air cooling.When aging at 870 ℃and 970 ℃,the size of M23C6 increases with the increase of temperature and aging time.
Keyword定向凝固co基合金 固溶 时效 碳化物
Subject Area力学
URL查看原文
Indexed ByCSCD
Language中文
CSCD IDCSCD:4425540
DepartmentLMFS多相流及流固耦合(LHO)
Citation statistics
Document Type期刊论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/45056
Collection水动力学与海洋工程重点实验室(2009-2011)
Corresponding Author孙跃军
Recommended Citation
GB/T 7714
孙跃军,林陌思,葛艳辉,等. 热处理对定向凝固Co基合金微观组织的影响[J]. 热加工工艺,2011,40(12):152-154,159.
APA 孙跃军,林陌思,葛艳辉,&张军.(2011).热处理对定向凝固Co基合金微观组织的影响.热加工工艺,40(12),152-154,159.
MLA 孙跃军,et al."热处理对定向凝固Co基合金微观组织的影响".热加工工艺 40.12(2011):152-154,159.
Files in This Item: Download All
File Name/Size DocType Version Access License
C2011J125.pdf(858KB) 开放获取--View Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[孙跃军]'s Articles
[林陌思]'s Articles
[葛艳辉]'s Articles
Baidu academic
Similar articles in Baidu academic
[孙跃军]'s Articles
[林陌思]'s Articles
[葛艳辉]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[孙跃军]'s Articles
[林陌思]'s Articles
[葛艳辉]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: C2011J125.pdf
Format: Adobe PDF
This file does not support browsing at this time
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.