激光熔覆Ta-W合金涂层工艺方法研究
Alternative TitleResearch on Processing of Laser Cladding Ta-W Alloy Coatings
武扬; 虞钢; 何秀丽; 宁伟健; 郑彩云; 张永杰
Source Publication中国激光
2011
Volume38Issue:8Pages:0803008-1-080300-6
ISSN0258-7025
Abstract采用预置涂层和同轴送粉激光熔覆方法,分别以Ta/W混合粉末和纯W粉末为熔覆材料,纯Ta为基底,在Ta板上制备Ta-W合金涂层,对难熔金属材料的激光熔覆工艺方法进行了对比研究。利用扫描电镜(SEM)、能谱仪(EDS)及显微硬度计对两种方法所制备熔覆层的微观组织和显微硬度进行了分析。结果表明,预置粉末法激光熔覆层厚度均匀,稀释率低,涂层内部为粗大的Ta-W合金固溶体组织,熔覆层平均硬度为1500HV,高于基底10倍。同轴送粉法激光熔覆层与基底呈良好的冶金结合,熔深较大,涂层内部为致密细小的树枝状Ta-W合金固溶体,均匀分布于Ta中。涂层平均硬度为800HV,为基材的5倍。
Other AbstractTa-W alloy coatings were deposited on pure Ta plate by laser cladding with pre-coating and coaxial powder injection respectively in order to find the effects with two technique.The microstructure of the coatings was analyzed using scanning electron microscopy(SEM) and energy dispersive spectroscopy(EDS).The microhardness was examined by hardness tester.The clad layer which formed with pre-coating had a microstructure of coarse columnar grain and low dilution rate with the substrate.The average microhardness of the clad layer was 1500 HV,it was 10 times greater than the Ta substrate.The clad layer deposited with coaxial power injection had a microstructure consisting of dendrite Ta-W solid solution uniformly dispersed in the Ta matrix.The average microhardness of the clad layer was approximately 800 HV and it was 5 times greater than that of the substrate.
Keyword激光技术 激光熔覆 预置粉末 同轴送粉 Ta-w合金 显微组织
Subject Area力学
URL查看原文
Indexed ByEI ; CSCD
Language中文
Funding Organization国家自然科学基金(10832011)资助课题
CSCD IDCSCD:4282631
DepartmentMAM激光智能制造工艺力学
Citation statistics
Cited Times:1[CSCD]   [CSCD Record]
Document Type期刊论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/45152
Collection先进制造工艺力学重点实验室
Corresponding Author武扬
Recommended Citation
GB/T 7714
武扬,虞钢,何秀丽,等. 激光熔覆Ta-W合金涂层工艺方法研究[J]. 中国激光,2011,38(8):0803008-1-080300-6
APA 武扬,虞钢,何秀丽,宁伟健,郑彩云,&张永杰.(2011).激光熔覆Ta-W合金涂层工艺方法研究.中国激光,38(8),0803008-1-080300-6.
MLA 武扬,et al."激光熔覆Ta-W合金涂层工艺方法研究".中国激光 38.8(2011):0803008-1-080300-6.
Files in This Item: Download All
File Name/Size DocType Version Access License
C2011J091.pdf(0KB) 开放获取--View Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[武扬]'s Articles
[虞钢]'s Articles
[何秀丽]'s Articles
Baidu academic
Similar articles in Baidu academic
[武扬]'s Articles
[虞钢]'s Articles
[何秀丽]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[武扬]'s Articles
[虞钢]'s Articles
[何秀丽]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: C2011J091.pdf
Format: Adobe PDF
This file does not support browsing at this time
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.