Very high cycle fatigue for GCr15 steel with smooth and hole-defect specimens
Lei ZQ(雷铮强); Zhao AG(赵爱国); Xie JJ(谢季佳); Sun CQ(孙成奇); Hong YS(洪友士)
Source PublicationTHEORETICAL & APPLIED MECHANICS LETTERS
2012-05-10
Volume2Issue:3Pages:031003
ISSN2095-0349
AbstractVery high cycle fatigue (VHCF) properties of a low temperature tempering bearing steel GCr15 with smooth and hole-defect specimens are studied by employing a rotary bending test machine with frequency of 52.5 Hz. Both smooth and hole-defect specimens break in VHCF regime with some difference in fatigue crack initiation. For smooth specimens, a fine granular area (FGA) is observed near the grain boundary in the fracture surface of the specimens broken after 10^7 cycles. But no FGA is observed in the hole-defect specimens broken in VHCF regime, and the VHCF crack does not initiate from the small hole at the surface as it does at low or high cycle fatigue regime. Internal stress is employed to explain the VHCF behavior of these two types of specimens. At last, an advanced dislocation model based on Tanaka and Mura model is proposed to illustrate the internal stress process and to predict fatigue crack initiation life with FGA observed in the fracture region.; Very high cycle fatigue (VHCF) properties of a low temperature tempering bearing steel GCr15 with smooth and hole-defect specimens are studied by employing a rotary bending test machine with frequency of 52.5 Hz. Both smooth and hole-defect specimens break in VHCF regime with some difference in fatigue crack initiation. For smooth specimens, a fine granular area (FGA) is observed near the grain boundary in the fracture surface of the specimens broken after 10^7 cycles. But no FGA is observed in the hole-defect specimens broken in VHCF regime, and the VHCF crack does not initiate from the small hole at the surface as it does at low or high cycle fatigue regime. Internal stress is employed to explain the VHCF behavior of these two types of specimens. At last, an advanced dislocation model based on Tanaka and Mura model is proposed to illustrate the internal stress process and to predict fatigue crack initiation life with FGA observed in the fracture region.
KeywordVery High Cycle Fatigue Gcr15 Fga Hole-defect Experimental Research
Subject Area疲劳与断裂力学
URL查看原文
Language英语
Funding OrganizationThis work was supported by the National Natural Science Foundation of China (11021262 and 11172304), and the National Basic Research Program of China (2012CB937500).
DepartmentLNM金属材料微结构与力学性能
Classification二类
Document Type期刊论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/46400
Collection非线性力学国家重点实验室
Corresponding AuthorHong YS(洪友士)
Recommended Citation
GB/T 7714
Lei ZQ,Zhao AG,Xie JJ,et al. Very high cycle fatigue for GCr15 steel with smooth and hole-defect specimens[J]. THEORETICAL & APPLIED MECHANICS LETTERS,2012,2(3):031003.
APA 雷铮强,赵爱国,谢季佳,孙成奇,&洪友士.(2012).Very high cycle fatigue for GCr15 steel with smooth and hole-defect specimens.THEORETICAL & APPLIED MECHANICS LETTERS,2(3),031003.
MLA 雷铮强,et al."Very high cycle fatigue for GCr15 steel with smooth and hole-defect specimens".THEORETICAL & APPLIED MECHANICS LETTERS 2.3(2012):031003.
Files in This Item: Download All
File Name/Size DocType Version Access License
C2012J-168.pdf(5185KB) 开放获取--View Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[雷铮强]'s Articles
[赵爱国]'s Articles
[谢季佳]'s Articles
Baidu academic
Similar articles in Baidu academic
[雷铮强]'s Articles
[赵爱国]'s Articles
[谢季佳]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[雷铮强]'s Articles
[赵爱国]'s Articles
[谢季佳]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: C2012J-168.pdf
Format: Adobe PDF
This file does not support browsing at this time
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.