激光熔覆Fe-W合金涂层的组织及性能

IMECH-IR > 先进制造工艺力学实验室

	激光熔覆Fe-W合金涂层的组织及性能
其他题名	Microstructure and properties of Fe-W composite coating by laser cladding
	武扬; 虞钢; 何秀丽; 宁伟健
发表期刊	焊接学报
	2012-02-25
卷号	33 期号:2 页码:40-44
ISSN	0253-360X
摘要	以纯钨粉末为熔覆材料,采用同轴送粉激光熔覆技术,在Q235A钢表面制备了Fe-W合金耐磨涂层.利用X射线衍射(XRD)、光学显微镜、扫描电镜(SEM)及能谱(EDS)对熔覆层的显微组织进行了分析,用显微硬度计和摩擦磨损试验机对熔覆层的硬度和耐磨性进行了测试.结果表明,熔覆层与基底冶金结合,无明显裂纹或气孔,涂层内部由致密的粗大树枝状和短棒状Fe_7W_6增强相以及弥散分布的细小颗粒状Fe_2W相组成,其均匀分布在α-Fe固溶体中.熔覆层平均硬度700 HV,为基材Q235A钢的3.5倍,同时耐磨性能也得到了显著提高.
其他摘要	An investigation of laser cladding Fe-W composite coating on Q235 steel was performed by injection of tungsten powder. The microstructure of the coating was analyzed with X-ray diffraction (XRD), optical microscope, scanning electron microscopy (SEM) and energy disperse spectroscopy (EDS). The microhardness and wear resistance were examined by hardness tester and abrading machine. The coating was metallurgically bonded with the substrate without visible crack or pore. The clad layer had a microstructure consisting of primary coarse dendrite or short stick Fe7W6 and fine isolated Fe2W particles which uniformly dispersed in the -Fe matrix. The average microhardness of the clad layer was approximately 700 HV which was 3.5 times greater than that of the Q235 substrate. The wear resistance was also obviously improved.
关键词	激光熔覆同轴送粉 Fe-w合金涂层显微硬度耐磨性
学科领域	制造工艺力学
URL	查看原文
收录类别	CSCD ; EI
语种	中文
项目资助者	国家自然科学基金重点资助项目(10832011)
CSCD记录号	CSCD:4632333
课题组名称	MAM激光智能制造工艺力学
引用统计
文献类型	期刊论文
条目标识符	http://dspace.imech.ac.cn/handle/311007/46414
专题	先进制造工艺力学实验室
通讯作者	虞钢
推荐引用方式 GB/T 7714	武扬,虞钢,何秀丽,等. 激光熔覆Fe-W合金涂层的组织及性能[J]. 焊接学报,2012,33,2,:40-44.
APA	武扬,虞钢,何秀丽,&宁伟健.(2012).激光熔覆Fe-W合金涂层的组织及性能.焊接学报,33(2),40-44.
MLA	武扬,et al."激光熔覆Fe-W合金涂层的组织及性能".焊接学报 33.2(2012):40-44.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
C2012J-087.pdf（3238KB）			开放获取	--	浏览下载