镍基单晶合金热处理过程中的组织演变
Alternative TitleMicrostructure Evolution of Ni-based Single Crystal Superalloy During Heat-treating
孙跃军; 葛艳辉; 张军
Source Publication热加工工艺
2012-01-25
Volume41Issue:2Pages:214-218
ISSN1001-3814
Abstract利用螺旋选晶法制备了镍基单晶合金,研究了热处理过程中合金的组织演变。结果表明:合金的铸态组织由枝晶组成,W偏析于枝晶干,Ti、Cr、Mo和Ta偏析于枝晶间,固溶处理可以消除铸态组织中的枝晶,减小成分偏析,固溶温度越高,粗大的γ’和γ/γ’共晶溶解的越完全。时效处理过程中,大尺寸的γ’发生粗化,小尺寸的γ’逐渐消失,时效温度越高,γ’粗化得越严重。热处理促进合金元素在γ和γ’中的均匀分布,减小了合金的错配度。
Other AbstractA Ni-based superalloy was prepared by screw selecting crystal method.Microstructure evolution of the alloy during heat-treatment was investigated.The results show that the as-casting microstructure is composed by dendrites.EDS analysis indicates that W partitioned in dendrite zone and Ti,Cr,Mo,Ta in inter-dendrite.Solid solution treatment decreases composition partitioning,and with the increase of the solution temperature,coarsening γ and γ/γ eutectic solves completely.During the aging treating,the larger...
Keyword镍基单晶合金 枝晶 固溶 时效 错配度
Subject Area新型材料的力学问题
URL查看原文
Indexed ByCSCD
Language中文
CSCD IDCSCD:4438456
DepartmentLMFS多相流及流固耦合(LHO)
Citation statistics
Cited Times:2[CSCD]   [CSCD Record]
Document Type期刊论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/46451
Collection流固耦合系统力学重点实验室
Corresponding Author孙跃军
Recommended Citation
GB/T 7714
孙跃军,葛艳辉,张军. 镍基单晶合金热处理过程中的组织演变[J]. 热加工工艺,2012,41(2):214-218.
APA 孙跃军,葛艳辉,&张军.(2012).镍基单晶合金热处理过程中的组织演变.热加工工艺,41(2),214-218.
MLA 孙跃军,et al."镍基单晶合金热处理过程中的组织演变".热加工工艺 41.2(2012):214-218.
Files in This Item: Download All
File Name/Size DocType Version Access License
C2012J-116.pdf(1097KB) 开放获取--View Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[孙跃军]'s Articles
[葛艳辉]'s Articles
[张军]'s Articles
Baidu academic
Similar articles in Baidu academic
[孙跃军]'s Articles
[葛艳辉]'s Articles
[张军]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[孙跃军]'s Articles
[葛艳辉]'s Articles
[张军]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: C2012J-116.pdf
Format: Adobe PDF
This file does not support browsing at this time
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.