激光熔覆Ta-W合金组织及高温气动烧蚀性能
Alternative TitleMicrostructure and high temperature aerodynamic ablation property of Ta-W alloy deposited by coaxial laser cladding
武扬; 虞钢; 何秀丽; 宁伟健; Wu, Y; Chinese Acad Sci, Key Lab Mech Adv Mfg, Inst Mech, Beijing 100190, Peoples R China.
Source Publication稀有金属材料与工程=Rare Metal Materials and Engineering
2012-07-15
Volume41Issue:7Pages:1211-1215
ISSN1002-185X
Abstract以纯W粉末为熔覆材料,纯Ta为基底,采用同轴送粉激光熔覆技术在Ta板侧面制备了Ta-W合金涂层。利用扫描电镜(SEM)、能谱(EDS)及显微硬度计对熔覆层的微观组织和显微硬度进行了分析,在直联式自由射流风洞试验台上对涂层的抗高温高速气流烧蚀性能进行了测试。结果表明,熔覆层与基底冶金结合,涂层内部为致密的树枝状Ta-W合金固溶体,大致均匀地分布于Ta中。Ta-W合金涂层平均HV硬度8GPa,为基材的5倍,同时抗烧蚀性能得到了显著提高。
Other AbstractA Ta-W alloy coating was deposited on pure Ta plate by coaxial laser cladding, using tungsten powder as cladding material. The microstructure of the coating was analyzed by scanning electron microscopy (SEM) and energy disperse spectroscopy (EDS). The microhardness was examined by hardness tester. The high temperature hypersonic flow ablation property was tested in the wind tunnel system. It is found that the coating is metallurgically bonded with the substrate. The clad layer has a microstructure consisting of dendrite Ta-W solid solution uniformly dispersed in the Ta matrix. The average microhardness of the clad layer is approximately 8 GPa and it is 5 times greater than that of the Ta substrate. The ablative property is also obviously improved.
Subject Area制造工艺力学
URL查看原文
Indexed BySCI ; EI ; CSCD
Language中文
WOS IDWOS:000308053900018
WOS KeywordMECHANICAL-PROPERTIES ; OXIDATION ; TANTALUM ; TUNGSTEN ; COATINGS
WOS Research AreaMaterials Science ; Metallurgy & Metallurgical Engineering
WOS SubjectMaterials Science, Multidisciplinary ; Metallurgy & Metallurgical Engineering
Funding Organization国家自然科学基金(10832011)
CSCD IDCSCD:4603557
DepartmentMAM激光智能制造工艺力学
Citation statistics
Cited Times:1[CSCD]   [CSCD Record]
Document Type期刊论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/46623
Collection先进制造工艺力学重点实验室
Corresponding AuthorWu, Y; Chinese Acad Sci, Key Lab Mech Adv Mfg, Inst Mech, Beijing 100190, Peoples R China.
Recommended Citation
GB/T 7714
武扬,虞钢,何秀丽,等. 激光熔覆Ta-W合金组织及高温气动烧蚀性能[J]. 稀有金属材料与工程=Rare Metal Materials and Engineering,2012,41(7):1211-1215
APA 武扬,虞钢,何秀丽,宁伟健,Wu, Y,&Chinese Acad Sci, Key Lab Mech Adv Mfg, Inst Mech, Beijing 100190, Peoples R China..(2012).激光熔覆Ta-W合金组织及高温气动烧蚀性能.稀有金属材料与工程=Rare Metal Materials and Engineering,41(7),1211-1215.
MLA 武扬,et al."激光熔覆Ta-W合金组织及高温气动烧蚀性能".稀有金属材料与工程=Rare Metal Materials and Engineering 41.7(2012):1211-1215.
Files in This Item: Download All
File Name/Size DocType Version Access License
SCI-J2012-222.pdf(5794KB) 开放获取--View Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[武扬]'s Articles
[虞钢]'s Articles
[何秀丽]'s Articles
Baidu academic
Similar articles in Baidu academic
[武扬]'s Articles
[虞钢]'s Articles
[何秀丽]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[武扬]'s Articles
[虞钢]'s Articles
[何秀丽]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: SCI-J2012-222.pdf
Format: Adobe PDF
This file does not support browsing at this time
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.