Uniaxial tensile and cross-sectional indentation tests to investigate the adhesion between the brittle Cr coating and the ductile steel substrate
Yang BQ(杨班权); Chen GN(陈光南); Chen XJ(陈学军); Yang BQ(杨班权)
Source PublicationADVANCES IN MECHANICAL ENGINEERING
2011
Pages854-858
Conference Name2011 1st International Conference on Mechanical Engineering, ICME 2011
Conference DateAPR 03-04, 2011
Conference PlacePhuket, Thailand
AbstractAdhesion of a coating on its substrate is a crucial parameter determining performance and reliability of coating-substrate system. In this work, the uniaxial tensile and cross-sectional indentation tests are used to investigate the adhesion between the brittle Cr coating and the ductile steel substrate. The uniaxial tensile test results show the maximum shear flow stress level of the ductile steel substrate can only serve as a lower bound estimate on the ultimate shear strength of the interface. The cross-sectional indentation test results show the interfacial decohesion does not occur prior to the cracking of the brittle Cr coating.
KeywordAdhesion Carbon Steel Mechanical Engineering Shear Flow Shear Strength Substrates Tensile Strength Tensile Testing Testing Coating-substrate Systems Cr Coating Cross-sectional Indentations Crucial Parameters Ductile Steel Substrate Flow Stress Interfacial Decohesion Lower Bounds Maximum Shears Normal Medium Carbon Steel Ultimate Shear Strength Uniaxial Tensile Test
DepartmentMAM表面与界面改性
ISBN978-3-03785-077-0
URL查看原文
Indexed ByEI
Language英语
Document Type会议论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/46840
Collection先进制造工艺力学重点实验室
Corresponding AuthorYang BQ(杨班权)
Recommended Citation
GB/T 7714
Yang BQ,Chen GN,Chen XJ,et al. Uniaxial tensile and cross-sectional indentation tests to investigate the adhesion between the brittle Cr coating and the ductile steel substrate[C]ADVANCES IN MECHANICAL ENGINEERING,2011:854-858.
Files in This Item: Download All
File Name/Size DocType Version Access License
AMM.52-54.854.pdf(246KB) 开放获取--View Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Yang BQ(杨班权)]'s Articles
[Chen GN(陈光南)]'s Articles
[Chen XJ(陈学军)]'s Articles
Baidu academic
Similar articles in Baidu academic
[Yang BQ(杨班权)]'s Articles
[Chen GN(陈光南)]'s Articles
[Chen XJ(陈学军)]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Yang BQ(杨班权)]'s Articles
[Chen GN(陈光南)]'s Articles
[Chen XJ(陈学军)]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: AMM.52-54.854.pdf
Format: Adobe PDF
This file does not support browsing at this time
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.