Research on interfacial cracking of a Cr coating/steel substrate with and without laser pre-quenching treatment under thermal fatigue loading

IMECH-IR > 先进制造工艺力学实验室

	Research on interfacial cracking of a Cr coating/steel substrate with and without laser pre-quenching treatment under thermal fatigue loading
	Yang BQ(杨班权); Chen GN(陈光南); Chen XJ(陈学军); Sun WH; Chen HQ; Pan JW; Chen Y; Yang BQ(杨班权)
会议录名称	DIGITAL MANUFACTURING AND AUTOMATION III
	2012
页码	543-546
会议名称	3rd International Conference on Digital Manufacturing and Automation, ICDMA 2012
会议日期	AUG 01-02, 2012
会议地点	Guangxi, China
摘要	The interfacial cracking behaviors of a chromium (Cr) coating/laser pre-quenched steel substrate system and a Cr coating/original steel substrate system under thermal fatigue loading were investigated in this work. The experiment results show that the Cr coating on the pre-quenched substrate surface exhibited a higher resistance of interfacial cracking than that of the Cr coating on the original substrate surface under the same loading condition. This indicates the technology of laser pre-quenching of steel substrate surface prior to plating the Cr coating can improve the interfacial adhesion properties between the coating and substrate.
关键词	Chromate Coatings Chromium Manufacture Quenching Substrates Thermal Fatigue Interfacial Adhesions Interfacial Cracking Loading Condition Steel Substrate Substrate Surface
WOS记录号	WOS:000311978100117
课题组名称	MAM表面与界面改性
URL	查看原文
收录类别	CPCI-S ; EI
语种	英语
引用统计
文献类型	会议论文
条目标识符	http://dspace.imech.ac.cn/handle/311007/46842
专题	先进制造工艺力学实验室
通讯作者	Yang BQ(杨班权)
推荐引用方式 GB/T 7714	Yang BQ,Chen GN,Chen XJ,et al. Research on interfacial cracking of a Cr coating/steel substrate with and without laser pre-quenching treatment under thermal fatigue loading[C]DIGITAL MANUFACTURING AND AUTOMATION III,2012:543-546.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
AMM.190-191.543.pdf（329KB）	会议论文		开放获取	CC BY-NC-SA	浏览下载