Novel high damage-tolerant, wear resistant MoSi2-based nanocomposite coatings
Xu J; Li ZY(李正阳); Xie ZH; Munroe P; Lu XL; Lan XF; Jiang Xu
Source PublicationAPPLIED SURFACE SCIENCE
2013-04-01
Volume270Pages:418-427
ISSN0169-4332
AbstractIn this study, novel MoSi2-based nanocomposite coatings were deposited on Ti-6Al-4V substrates by a two-step process involving firstly, deposition of MoSi2-based coatings, using a double cathode glow discharge process and, secondly, plasma nitridation of the as-deposited coatings. The aim of this latter step is to introduce nitrogen into the coating and promote the formation of amorphous silicon nitride. The resulting coatings were characterized by X-ray diffraction (XRD), X-ray photoelectron spectroscope (XPS), transmission electron microscopy (TEM) and scanning electron microscopy (SEM). It was found that the nanocomposite coatings were composed of nanocrystallite Mo5Si3 and MoSi2 grains embedded in an amorphous Si3N4 matrix. The mechanical properties and damage resistance of the coatings were evaluated by both Vickers indentation and nanoindentation techniques. Dry sliding wear tests were performed using a ball-on-disc type tribometer, in which the coated samples were tested against a ZrO2 ceramic ball at normal loads of 2.8 and 4.3 N under ambient conditions. Compared with the monolithic MoSi2 nanocrystalline coating, the specific wear rates of the  nanocomposite coatings decreased by an order of magnitude. The specific wear rate was further improved by about 20% through the addition of Al, which was attributed to an optimum combination of mechanical properties.
KeywordNanocomposites Mechanical Properties Wear Coatings
Subject Area损伤、破坏机理和微结构演化
URL查看原文
Indexed BySCI ; EI
Language英语
WOS IDWOS:000316790200063
Funding OrganizationThe authors acknowledge the financial support of the National Natural Science Foundation of China under grant No. 51175245.
DepartmentMAMYAG激光毛化技术
Classification一类
Citation statistics
Cited Times:8[WOS]   [WOS Record]     [Related Records in WOS]
Document Type期刊论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/47120
Collection先进制造工艺力学重点实验室
Corresponding AuthorJiang Xu
Recommended Citation
GB/T 7714
Xu J,Li ZY,Xie ZH,et al. Novel high damage-tolerant, wear resistant MoSi2-based nanocomposite coatings[J]. APPLIED SURFACE SCIENCE,2013,270:418-427.
APA Xu J.,Li ZY.,Xie ZH.,Munroe P.,Lu XL.,...&Jiang Xu.(2013).Novel high damage-tolerant, wear resistant MoSi2-based nanocomposite coatings.APPLIED SURFACE SCIENCE,270,418-427.
MLA Xu J,et al."Novel high damage-tolerant, wear resistant MoSi2-based nanocomposite coatings".APPLIED SURFACE SCIENCE 270(2013):418-427.
Files in This Item: Download All
File Name/Size DocType Version Access License
IMCAS-J2013-084.pdf(2014KB)期刊论文作者接受稿开放获取CC BY-NC-SAView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Xu J]'s Articles
[Li ZY(李正阳)]'s Articles
[Xie ZH]'s Articles
Baidu academic
Similar articles in Baidu academic
[Xu J]'s Articles
[Li ZY(李正阳)]'s Articles
[Xie ZH]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Xu J]'s Articles
[Li ZY(李正阳)]'s Articles
[Xie ZH]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: IMCAS-J2013-084.pdf
Format: Adobe PDF
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.