| In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer during Surface Mechanical Attrition Treatment of Zirconium | |
Sun CY(孙彩云) ; Xie JJ(谢季佳); Wu XL(武晓雷); Hong YS(洪友士); Liu G; Lu J; Lu K
| |
| Source Publication | 材料热处理学报
 |
| 2004 | |
| Volume | 25Issue:5IIPages:1242-1246 |
| ISSN | 1009-6264 |
| Abstract | The surface mechanical attrition treatment (SMAT) technique was developed to synthesize a nanocrystalline (NC)layer on the surface of metallic materials for upgrading their overall properties and performance. In this paper, by means of SMAT to a pure zirconium plate at the room temperature, repetitive multidirectional peening of steel shots (composition (wt%): 1C, 1.5Cr, base Fe) severely deformed the surface layer. A NC surface layer consisting of the intermetallic compound FeCr was fabricated on the surface of the zirconium. The microstructure characterization of the surface layer was performed by using X-ray diffraction analysis, optical microscopy, scanning and transmission electron microscopy observations. The NC surface layer was about 25 μm thick and consisted of the intermetallic compound FeCr with an average grain size of 25+10 nm. The deformation-induced fast diffusion of Fe and Cr from the steel shots into Zr occurred during SMAT, leading to the formation of intermetallic compound. In addition, the NC surface layer exhibited an ultrahigh nanohardness of 10.2 GPa. |
| Keyword | Nanocrystalline Intermetallic Compound Surface Layer Deformation Diffusion |
| Indexed By | EI ; CSCD |
| Language | 中文 |
| CSCD ID | CSCD:1847864 |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://dspace.imech.ac.cn/handle/311007/47743 |
| Collection | 力学所知识产出(1956-2008) |
| Recommended Citation GB/T 7714 | Sun CY,Xie JJ,Wu XL,et al. In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer during Surface Mechanical Attrition Treatment of Zirconium[J]. 材料热处理学报,2004,25(5II):1242-1246. |
| APA | Sun CY.,Xie JJ.,Wu XL.,Hong YS.,Liu G.,...&Lu K.(2004).In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer during Surface Mechanical Attrition Treatment of Zirconium.材料热处理学报,25(5II),1242-1246. |
| MLA | Sun CY,et al."In Situ Synthesis of Nanocrystalline Intermetallic Compound Layer during Surface Mechanical Attrition Treatment of Zirconium".材料热处理学报 25.5II(2004):1242-1246. |
| Files in This Item: | Download All | |||||
| File Name/Size | DocType | Version | Access | License | ||
| InSituSynthesiso_tme（541KB） | 开放获取 | License | View Download | |||
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment