Research on fracture behavior of a Cr coating/original steel substrate material under thermal fatigue loading
Yang BQ(杨班权); Chen GN(陈光南); Du J; Chen XJ(陈学军); Sun WH; Chen HQ; Pan JW; Chen Y; Yang BQ(杨班权)
Source PublicationMechanical Engineering, Materials Science and Civil Engineering II
2014
Pages146-149
Conference Name2nd International Conference on Mechanical Engineering, Materials Science and Civil Engineering, ICMEMSCE 2013
Conference DateOCT 25-26, 2013
Conference PlaceBeijing, China
AbstractThe facture behavior of a chromium (Cr) coating/ original steel substrate material was investigated in this work. The results presented in this work show the crack density of the Cr coating on the substrate increases with the increase of the thermal fatigue times, and the failure process and modes of the Cr coating /original steel substrate system can be described as follows: Firstly, the micro-cracks of the coating grew and interconnected as the thermal fatigue time increased. Secondly, the "pocket" cracking at the coating and the substrate interface occurred, and the main cracks of the coating formed. Finally, the spallation or (and) collapse of the coating occurred.
DepartmentMAM表面与界面改性
ISBN9783037859612
URL查看原文
Indexed ByEI
Language英语
Document Type会议论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/48264
Collection先进制造工艺力学实验室
Corresponding AuthorYang BQ(杨班权)
Recommended Citation
GB/T 7714
Yang BQ,Chen GN,Du J,et al. Research on fracture behavior of a Cr coating/original steel substrate material under thermal fatigue loading[C]Mechanical Engineering, Materials Science and Civil Engineering II,2014:146-149.
Files in This Item: Download All
File Name/Size DocType Version Access License
yang2013.pdf(416KB)会议论文 开放获取CC BY-NC-SAView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Yang BQ(杨班权)]'s Articles
[Chen GN(陈光南)]'s Articles
[Du J]'s Articles
Baidu academic
Similar articles in Baidu academic
[Yang BQ(杨班权)]'s Articles
[Chen GN(陈光南)]'s Articles
[Du J]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Yang BQ(杨班权)]'s Articles
[Chen GN(陈光南)]'s Articles
[Du J]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: yang2013.pdf
Format: Adobe PDF
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.