| Role of Cr additions in enhancing wear and oxidation resistance of (Mo1-xCrx)Si-2 nanocrystalline films | |
Xu J; Li ZY(李正阳) ; Munroe P; Xie ZH; Xu, J (reprint author), Nanjing Univ Aeronaut & Astronaut, Dept Mat Sci & Engn, 29 Yudao St, Nanjing 210016, Jiangsu, Peoples R China.
| |
| 发表期刊 | CERAMICS INTERNATIONAL
 |
| 2014-12 | |
| 卷号 | 40期号:10页码:15859-15874 |
| ISSN | 0272-8842 |
| 摘要 | In order to explore the effects of Cr alloying on the wear and oxidation resistance of MoSi2 films, four kinds of (Mo1-xCrx)Si-2 (x=0, 0.05, 0.10 and 0.15) nanocrystalline films of differing Cr contents were fabricated onto Ti6Al4V substrates by a double cathode glow discharge apparatus. The microstructure features of the as-deposited films were characterized by X-ray diffraction (XRD), field-emission scanning electron microscopy (FESEM) and transmission electron microscopy (TEM). The hardness and elastic modulus of the (Mo1-xCrx)Si-2 nanocrystalline films were evaluated by nano-indentation. The dry sliding wear properties of the as-deposited films sliding against GCr15 rolling bearing steel were studied using a ball-on-disc type tribometer at room temperature. The results showed that the friction coefficients and specific wear rates of the (Mo1-xCrx)Si-2 nanocrystalline films decreased with increasing Cr content in the films. The oxidation behavior of the (Mo1-xCrx)Si-2 nanocrystalline films was investigated at 500 degrees C under cyclic oxidation conditions in air for exposure time of 100 h. The oxidation kinetics of the films was found to obey a subparabolic behavior, and three Cr-containing MoSi2 films showed a much lower weight gain and the oxidation rate constant as compared to the monolithic MoSi2 film during a 100 h exposure. Surface morphologies, phase constituents and electrochemical behavior of the oxide scales formed on the (Mo1-xCrx)Si-2 nanocrystalline films were characterized using FESEM, XRD and electrochemical-impedance spectroscopy (EIS). The electrochemical results revealed that the structure of the oxide scales changed from a homogeneous and dense structure to a duplex structure consisting of a porous outer layer and a denser inner layer. The overall resistance of the oxide scales depended strongly on both the oxidation time and Cr content in the films. (C) 2014 Elsevier Ltd and Techna Group S.r.l. All rights reserved. |
| 关键词 | Molybdenum Silicides Oxidation Behavior Friction And Wear Electrochemical Impedance Spectroscopy |
| 学科领域 | Materials Science |
| URL | 查看原文 |
| 收录类别 | SCI ; EI |
| 语种 | 英语 |
| WOS记录号 | WOS:000343353600058 |
| 项目资助者 | The authors acknowledge the financial support of the National Natural Science Foundation of China under Grant nos. 51175245 and 51374130 and the Aeronautics Science Foundation of China under Grant no. 2013ZE52058. |
| 课题组名称 | MAMYAG激光毛化技术 |
| 论文分区 | 一类 |
| 引用统计 | |
| 文献类型 | 期刊论文 |
| 条目标识符 | http://dspace.imech.ac.cn/handle/311007/49353 |
| 专题 | 先进制造工艺力学实验室 |
| 通讯作者 | Xu, J (reprint author), Nanjing Univ Aeronaut & Astronaut, Dept Mat Sci & Engn, 29 Yudao St, Nanjing 210016, Jiangsu, Peoples R China. |
| 推荐引用方式 GB/T 7714 | Xu J,Li ZY,Munroe P,et al. Role of Cr additions in enhancing wear and oxidation resistance of (Mo1-xCrx)Si-2 nanocrystalline films[J]. CERAMICS INTERNATIONAL,2014,40,10,:15859-15874. |
| APA | Xu J,Li ZY,Munroe P,Xie ZH,&Xu, J .(2014).Role of Cr additions in enhancing wear and oxidation resistance of (Mo1-xCrx)Si-2 nanocrystalline films.CERAMICS INTERNATIONAL,40(10),15859-15874. |
| MLA | Xu J,et al."Role of Cr additions in enhancing wear and oxidation resistance of (Mo1-xCrx)Si-2 nanocrystalline films".CERAMICS INTERNATIONAL 40.10(2014):15859-15874. |
| 条目包含的文件 | 下载所有文件 | |||||
| 文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
| IMCAS-J2014-287.pdf（6234KB） | 开放获取 | -- | 浏览 下载 | |||
除非特别说明，本系统中所有内容都受版权保护，并保留所有权利。
修改评论