Characteristics of crack interior initiation and early growth originated from inclusion for very-high-cycle fatigue of high strength steels
Hong YS(洪友士); Lei ZQ(雷铮强); Sun CQ(孙成奇); Zhao AG(赵爱国)
Source PublicationProceedings of the 4th International Conference on CRACK PATHS (CP 2012) Gaeta (Italy), 9 – 21 September, 2012
2012-09
Conference NameThe 4th International Conference on “Crack Paths” (CP 2012)
Conference Date2012-09-09~09-21
Conference PlaceGaeta, Italy
Abstract
Fatigue tests on a high carbon chromium steel were performed with rotating bending and ultrasonic fatigue tests. The fractography was examined to reveal that fatigue cracks initiated at specimen interior for very-high-cycle fatigue (VHCF) with fish-eye pattern embracing fine-granular-area (FGA) morphology originated from inclusions. The measurements show the dimensions of FGA and fish-eye as a function of the applied stress and fatigue failure cycles. The results also show the values of stress intensity factor range at FGA (ΔKFGA) and fish-eye (ΔKfisheye) almost keep constant with failure cycles, and the values of ΔKFGA are close to the relevant fatigue threshold (ΔKth).
The fatigue life from FGA to fish-eye and from fish-eye to the critical crack size is respectively calculated, thus to estimate the fatigue life contributed by FGA. Moreover, the crack growth rate within FGA was estimated. The present result is combined with our previous ones and with those available in literature to discuss the process of crack initiation and early growth for VHCF, which is responsible for a majority part of total fatigue life. In addition, the large scattering of fatigue life was investigated, which was ascribed to the distribution of inclusion size.
;
DepartmentLNM金属材料微结构与力学性能
Language英语
Document Type会议论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/52731
Collection非线性力学国家重点实验室
Recommended Citation
GB/T 7714
Hong YS,Lei ZQ,Sun CQ,et al. Characteristics of crack interior initiation and early growth originated from inclusion for very-high-cycle fatigue of high strength steels[C]Proceedings of the 4th International Conference on CRACK PATHS (CP 2012) Gaeta (Italy), 9 – 21 September, 2012,2012.
Files in This Item: Download All
File Name/Size DocType Version Access License
CP931.pdf(405KB)会议论文 开放获取CC BY-NDView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Google Scholar
Similar articles in Google Scholar
[Hong YS(洪友士)]'s Articles
[Lei ZQ(雷铮强)]'s Articles
[Sun CQ(孙成奇)]'s Articles
Baidu academic
Similar articles in Baidu academic
[Hong YS(洪友士)]'s Articles
[Lei ZQ(雷铮强)]'s Articles
[Sun CQ(孙成奇)]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[Hong YS(洪友士)]'s Articles
[Lei ZQ(雷铮强)]'s Articles
[Sun CQ(孙成奇)]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: CP931.pdf
Format: Adobe PDF
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.