Evolution Mechanisms of Thermal Shock Cracks in Ceramic Sheet

doi:10.1115/1.4033175

IMECH-IR > 非线性力学国家重点实验室

	Evolution Mechanisms of Thermal Shock Cracks in Ceramic Sheet
	Xu XH(许向红); Lin ZK; Sheng SL; Yuan WJ; Xu, XH (reprint author), Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, 15 Beisihuanxi Rd, Beijing 100190, Peoples R China.
发表期刊	JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME
	2016
卷号	83 期号:7 页码:71001
ISSN	0021-8936
摘要	Knowledge of crack initiation, propagation, and corresponding thermal shock failure evolution is prerequisite for effective maintenance of civil engineering so as to avoid disaster. Experimental analysis of the cracking in the ceramic sheets subsequent to water quenching has been conducted. Based on statistical mesoscopic damage mechanics, it was revealed that there are four stages in the process of thermal shock evolution of ceramics subjected to water quenching. The multiple cracks interaction mechanism has been analyzed from the viewpoint of the evolution of the elastic strain energy and stress intensity factor.
关键词	Ceramic Thermal Shock Heterogeneity Crack Interaction Depth Grading
DOI	10.1115/1.4033175
URL	查看原文
收录类别	SCI ; EI
语种	英语
WOS记录号	WOS:000378407800001
关键词[WOS]	ceramic ; thermal shock ; heterogeneity ; crack interaction ; depth grading
WOS研究方向	Mechanics
WOS类目	Mechanics
项目资助者	The authors are grateful for the support from the National Natural Science Foundation of China through Grant No. 11272313.
课题组名称	LNM生物材料微结构和力学性能
论文分区	一类
力学所作者排名	True
引用统计	被引频次：4[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://dspace.imech.ac.cn/handle/311007/59541
专题	非线性力学国家重点实验室
通讯作者	Xu, XH (reprint author), Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, 15 Beisihuanxi Rd, Beijing 100190, Peoples R China.
推荐引用方式 GB/T 7714	Xu XH,Lin ZK,Sheng SL,et al. Evolution Mechanisms of Thermal Shock Cracks in Ceramic Sheet[J]. JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME,2016,83,7,:71001.
APA	许向红,Lin ZK,Sheng SL,Yuan WJ,&Xu, XH .(2016).Evolution Mechanisms of Thermal Shock Cracks in Ceramic Sheet.JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME,83(7),71001.
MLA	许向红,et al."Evolution Mechanisms of Thermal Shock Cracks in Ceramic Sheet".JOURNAL OF APPLIED MECHANICS-TRANSACTIONS OF THE ASME 83.7(2016):71001.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
a2016-085.pdf（2746KB）	期刊论文	作者接受稿	开放获取	CC BY-NC-SA	浏览下载