Research on fracture behavior of a Cr coating/ laser pre-quenched steel substrate system under thermal fatigue loading
Yang BQ(杨班权); Chen GN(陈光南); Chen XJ; Sun WH; Chen HQ; Pan JW; Chen Y
Source PublicationApplied Mechanics and Materials
2014
Conference NameInternational Conference on Vehicle and Mechanical Engineering and Information Technology, VMEIT 2014
Conference DateFebruary 19, 2014 - February 20, 2014
Conference PlaceBeijing, China
AbstractThe facture behavior of a chromium (Cr) coating/ laser pre-quenched steel substrate system was investigated in this work. The results presented in this work show the crack density of the Cr coating on the laser pre-quenched steel substrate increases with the increase of the thermal fatigue times, and the failure process and modes of the Cr coating/laser pre-quenched steel substrate are the same as those presented in our previous work. However, the crack density of Cr coating on the pre-quenched substrate surface was much lower than that of the Cr coating on the original substrate surface under the same thermal fatigue loading. This indicates the Cr coating on the pre-quenched steel substrate has superior mechanical properties than that on the original steel substrate. © (2014) Trans Tech Publications, Switzerland.
KeywordCr Coating/laser Pre-quenched Steel Substrate Systems Cr Coatings Crack Density Failure Process Fracture Behavior Steel Substrate Substrate Surface Thermal Fatigue Loadings
DepartmentMAMYAG激光毛化技术
ISBN9783038350606
URL查看原文
Indexed ByEI
Language英语
Document Type会议论文
Identifierhttp://dspace.imech.ac.cn/handle/311007/60238
Collection先进制造工艺力学实验室
Recommended Citation
GB/T 7714
Yang BQ,Chen GN,Chen XJ,et al. Research on fracture behavior of a Cr coating/ laser pre-quenched steel substrate system under thermal fatigue loading[C]Applied Mechanics and Materials,2014.
Files in This Item: Download All
File Name/Size DocType Version Access License
Cp2014-045.pdf(340KB)会议论文 开放获取CC BY-NC-SAView Download
Related Services
Recommend this item
Bookmark
Usage statistics
Export to Endnote
Lanfanshu
Similar articles in Lanfanshu
[杨班权]'s Articles
[陈光南]'s Articles
[Chen XJ]'s Articles
Baidu academic
Similar articles in Baidu academic
[杨班权]'s Articles
[陈光南]'s Articles
[Chen XJ]'s Articles
Bing Scholar
Similar articles in Bing Scholar
[杨班权]'s Articles
[陈光南]'s Articles
[Chen XJ]'s Articles
Terms of Use
No data!
Social Bookmark/Share
File name: Cp2014-045.pdf
Format: Adobe PDF
All comments (0)
No comment.
 

Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.