Analysis of resistance cracking process on the experiment of meso and macroscopic of quasi-brittle materials

IMECH-IR > 非线性力学国家重点实验室

	Analysis of resistance cracking process on the experiment of meso and macroscopic of quasi-brittle materials
	Wang LM 1; Xu SL 2; Wang HY(汪海英)3 ; Zhang DH 4
会议录名称	13th International Conference on Fracture 2013, ICF 2013
	2013
页码	3570-3577
会议名称	13th International Conference on Fracture 2013, ICF 2013
会议日期	June 16, 2013 - June 21, 2013
会议地点	Beijing, China
摘要	Engineering materials such as cast iron and concrete are quasi-brittle materials, and there is a fracture process zone in front of opening crack and it exist micro and macro defect and energy dissipation. The damage development area is simplified into fictitious crack, and its action stress distribution and opening displacement or deformation are along the cohesive crack. In order to investigate the constitutive relation of cohesive crack opening displacement and its stress distribution in quasi brittle materials, cast iron and concrete were used to test their fracture process by electronic equipment and micro view experiment facility. Through the analytical method of applied mathematics and mechanics, the material deformation stress constitutive relations were gotten for the cohesive crack. The theoretical calculation and test results are basically in agreement with each other. From the fracture criterion of Double K and the mechanics model of cohesive crack, the bearing capacity of structure with crack was estimated in this present paper. Copyright © (2013) by International Conference on Fracture.
关键词	Brittleness Cast iron Concretes Cracks Deformation Energy dissipation Fracture testing Inverse problems Materials testing Oscillators (electronic) Stress concentration Cohesive cracks Constitutive relations Engineering materials Fracture process Fracture process zone Mesoscopics Quasibrittle material Theoretical calculations
ISBN号	9781629933696
收录类别	EI
语种	英语
文献类型	会议论文
条目标识符	http://dspace.imech.ac.cn/handle/311007/77986
专题	非线性力学国家重点实验室
作者单位	1.Department of Science, Qingdao Technological University, Qingdao Shandong 266033, China; 2.Constructure Engineering School, Zhejiang University, Hangzhou Zhejinag 310058, China; 3.Chinese Academy of Sciences, Institute of Mechanics, Beijing 100190, China; 4.School of Transportation and Vehicle Engineering, Shandong University of Technology, Zibo 255049, China
推荐引用方式 GB/T 7714	Wang LM,Xu SL,Wang HY,et al. Analysis of resistance cracking process on the experiment of meso and macroscopic of quasi-brittle materials[C]13th International Conference on Fracture 2013, ICF 2013,2013:3570-3577.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
EiCpA011.pdf（711KB）	会议论文		开放获取	CC BY-NC-SA	浏览下载