Evaluation of Radiation Response in CoCrFeCuNi High-Entropy Alloys | |
Wang Y; Zhang K(张坤); Feng YH(冯义辉); Li YS; Tang WQ; Wei BC(魏炳忱) | |
发表期刊 | ENTROPY |
2018-11-01 | |
卷号 | 20期号:11页码:Ar-835 |
ISSN | 1099-4300 |
摘要 | CoCrFeCuNi high-entropy alloys (HEAs) prepared by arc melting were irradiated with a 100 keV He+ ion beam. Volume swelling and hardening induced by irradiation were evaluated. When the dose reached 5.0 x 10(17) ions/cm(2), the Cu-rich phases exhibited more severe volume swelling compared with the matrix phases. This result indicated that the Cu-rich phases were favorable sites for the nucleation and gathering of He bubbles. X-ray diffraction indicated that all diffraction peak intensities decreased regularly. This reduction suggested loosening of the irradiated layer, thereby reducing crystallinity, under He+ ion irradiation. The Nix-Gao model was used to fit the measured hardness in order to obtain a hardness value H-0 that excludes the indentation size effect. At ion doses of 2.5 x 10(17) ions/cm(2) and 5.0 x 10(17) ions/cm(2), the HEAs showed obvious hardening, which could be attributed to the formation of large amounts of irradiation defects. At the ion dose of 1.0 x 10(18) ions/cm(2), hardening was reduced, owing to the exfoliation of the original irradiation layer, combined with recovery induced by long-term thermal spike. This study is important to explore the potential uses of HEAs under extreme irradiation conditions. |
关键词 | high-entropy alloy ion irradiation hardening behavior volume swelling |
DOI | 10.3390/e20110835 |
URL | 查看原文 |
收录类别 | SCI |
语种 | 英语 |
WOS记录号 | WOS:000451308800027 |
关键词[WOS] | PRINCIPAL-ELEMENT ALLOYS ; ION-IRRADIATION ; FATIGUE BEHAVIOR ; SOLID-SOLUTION ; VISCOUS-FLOW ; HELIUM ; NANOINDENTATION ; MICROSTRUCTURE ; TEMPERATURE ; RELAXATION |
WOS研究方向 | Physics, Multidisciplinary |
WOS类目 | Physics |
项目资助者 | National Natural Science Foundation of China [51401028, 51271193, 11402277, 11790292] ; Strategic Priority Research Program of the Chinese Academy of Sciences [XDB22040303] |
论文分区 | 二类 |
力学所作者排名 | 1 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://dspace.imech.ac.cn/handle/311007/78153 |
专题 | 微重力重点实验室 非线性力学国家重点实验室 |
作者单位 | 1.Chinese Acad Sci, Inst Mech, Key Lab Micrograv, Natl Micrograv Lab, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, Sch Engn Sci, Beijing 100049, Peoples R China 3.Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China |
推荐引用方式 GB/T 7714 | Wang Y,Zhang K,Feng YH,et al. Evaluation of Radiation Response in CoCrFeCuNi High-Entropy Alloys[J]. ENTROPY,2018,20,11,:Ar-835. |
APA | Wang Y,张坤,冯义辉,Li YS,Tang WQ,&魏炳忱.(2018).Evaluation of Radiation Response in CoCrFeCuNi High-Entropy Alloys.ENTROPY,20(11),Ar-835. |
MLA | Wang Y,et al."Evaluation of Radiation Response in CoCrFeCuNi High-Entropy Alloys".ENTROPY 20.11(2018):Ar-835. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
irJ2018082.pdf(3503KB) | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 | |
IrJ2018376.pdf(3503KB) | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | 浏览 下载 |
个性服务 |
推荐该条目 |
保存到收藏夹 |
查看访问统计 |
导出为Endnote文件 |
Lanfanshu学术 |
Lanfanshu学术中相似的文章 |
[Wang Y]的文章 |
[张坤]的文章 |
[冯义辉]的文章 |
百度学术 |
百度学术中相似的文章 |
[Wang Y]的文章 |
[张坤]的文章 |
[冯义辉]的文章 |
必应学术 |
必应学术中相似的文章 |
[Wang Y]的文章 |
[张坤]的文章 |
[冯义辉]的文章 |
相关权益政策 |
暂无数据 |
收藏/分享 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论