The influence of combined gradient structure with residual stress on crack-growth behavior in medium carbon steel

doi:10.1016/j.engfracmech.2019.01.037

IMECH-IR > 非线性力学国家重点实验室

	The influence of combined gradient structure with residual stress on crack-growth behavior in medium carbon steel
	Wang Y(王瑶); Yuan LC ; Zhang SJ(张诗嘉); Sun CQ(孙成奇); Wang WJ ; Yang GX ; Li Q; Wei YJ(魏宇杰)
发表期刊	ENGINEERING FRACTURE MECHANICS
	2019-03-15
卷号	209 页码:369-381
ISSN	0013-7944
摘要	Gradient materials produced by various external surface treatments are widely used in various mechanical structures. In this study, we illustrated how the combined gradient structure and residual stress influences crack-tip plasticity and crack-growth behavior in medium carbon steel S38C. The material used as train axles has a gradient layer of thickness about 8 mm, with fine nanoscale structures in the surface to microstructures of tens of micron in the core. From the surface, the strength in the gradient layer decreases from about 1600 MPa to about 400 MPa, and the corresponding tensile ductility increases from 2% to 13%. Through in-situ fatigue tests, we further revealed slower crack-initiation and faster crack-growth rate in the gradient samples in contrast to their gradient-free coarse-grain counterparts. Using the key material parameters obtained from experiments, we employed finite-element simulations to examine the crack-growth behavior in the gradient structure with compressive residual stress. We showed that both the gradient structure and compressive residual stress reduce the plastic deformation size and hence slow down crack initiation. However, the lower ductility in the high strength gradient layer gives rise to even faster crack growth after the formation of a sharp crack. Based on the definition of the cyclic Delta J-integral for small scale yielding, we saw lower Delta J in the presence of the residual stress distribution, hence smaller driving force for the crack-growth rate as the latter monotonically increases with Delta J.
关键词	Gradient material Residual stress Fatigue crack Cyclic J-integral Crack- growth rate
DOI	10.1016/j.engfracmech.2019.01.037
收录类别	SCI ; EI
语种	英语
WOS记录号	WOS:000458750800024
关键词[WOS]	AUSTENITIC STAINLESS-STEEL ; HIGH-STRENGTH ; SURFACE-LAYER ; MECHANICAL-PROPERTIES ; FATIGUE LIFE ; HIGH-CYCLE ; GRAIN-SIZE ; PLASTICITY ; MICROSTRUCTURE ; RESISTANCE
WOS研究方向	Mechanics
WOS类目	Mechanics
项目资助者	National Natural Science Foundation of China (NSFC) [11425211] ; Strategic Priority Research Program of the Chinese Academy of Sciences [XDB22020200] ; Key Projects in the National Science & Technology Pillar Program [2015BAG12B01-01] ; National Key R&D Program of China [2018YFB1201704-04] ; Basic Scientific Research Foundation of Beijing Jiaotong University [M14JB00130]
论文分区	二类/Q1
力学所作者排名	1
RpAuthor	Wei, YJ ; Li, Q
引用统计	被引频次：29[WOS] [WOS记录] [WOS相关记录]
文献类型	期刊论文
条目标识符	http://dspace.imech.ac.cn/handle/311007/78456
专题	非线性力学国家重点实验室
作者单位	1.{Wang, Yao、Yuan, Lichao、Zhang, Shijia、Sun, Chengqi、Wei, Yujie} Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech LNM, Beijing 100190, Peoples R China 2.{Wang, Yao、Wang, Wenjing、Yang, Guangxue、Li, Qiang} Beijing Jiaotong Univ, Minist Educ, Key Lab Vehicle Adv Mfg Measuring & Control Techn, Beijing 100044, Peoples R China 3.{Wei, Yujie} Univ Chinese Acad Sci, Sch Engn Sci, Beijing 100049, Peoples R China 4.{Yuan, Lichao} Univ Chinese Acad Sci, Sch Future Technol, Beijing 100049, Peoples R China
推荐引用方式 GB/T 7714	Wang Y,Yuan LC,Zhang SJ,et al. The influence of combined gradient structure with residual stress on crack-growth behavior in medium carbon steel[J]. ENGINEERING FRACTURE MECHANICS,2019,209:369-381.
APA	王瑶.,Yuan LC.,张诗嘉.,孙成奇.,Wang WJ.,...&魏宇杰.(2019).The influence of combined gradient structure with residual stress on crack-growth behavior in medium carbon steel.ENGINEERING FRACTURE MECHANICS,209,369-381.
MLA	王瑶,et al."The influence of combined gradient structure with residual stress on crack-growth behavior in medium carbon steel".ENGINEERING FRACTURE MECHANICS 209(2019):369-381.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
Jp2019033.pdf（2613KB）	期刊论文	出版稿	开放获取	CC BY-NC-SA	浏览下载