Research on interfacial cracking of a Cr coating/steel substrate with and without laser pre-quenching treatment under thermal fatigue loading 会议论文
3rd International Conference on Digital Manufacturing and Automation, ICDMA 2012, Guangxi, China, AUG 01-02, 2012
作者:  Yang BQ(杨班权);  Chen GN(陈光南);  Chen XJ(陈学军);  Sun WH;  Chen HQ;  Pan JW;  Chen Y;  Yang BQ(杨班权)
浏览  |  Adobe PDF(329Kb)  |  收藏  |  浏览/下载：1044/192  |  提交时间：2013/02/26
Chromate Coatings  Chromium  Manufacture  Quenching  Substrates  Thermal Fatigue  Interfacial Adhesions  Interfacial Cracking  Loading Condition  Steel Substrate  Substrate Surface  
Interface delamination of the thermal barrier coating subjected to local heating 期刊论文
Science China Technological Sciences, 2010, 卷号: 53, 期号: 12, 页码: 3168-3174
作者:  Wu CW(吴臣武);  Huang CG(黄晨光);  Chen GN(陈光南)
Adobe PDF(960Kb)  |  收藏  |  浏览/下载：1150/256  |  提交时间：2010/12/28
tbc  Local Heating  Interface Delamination  Fe Modeling  
Interface Fracture Behavior Of Electroplated Coating On Metal Substrate Under Compressive Strain 期刊论文
Journal of Materials Processing Technology, 2009, 卷号: 209, 期号: 3, 页码: 1337-1341
作者:  Zhang K(张凯);  Zhang K(张坤);  Li HX(李怀学);  Chen GN(陈光南);  Zhang K
Adobe PDF(619Kb)  |  收藏  |  浏览/下载：1062/167  |  提交时间：2009/08/03
Electroplated Coating  Interface Fracture  Compressive Strain  T-bend Test  
On The Cyclic Bending Behaviour Of A Hard Coating On A Ductile Substrate With Periodic Surface Hardened Regions 期刊论文
International Journal of Solids and Structures, 2008, 页码: 5661-5674
作者:  Wu CW(吴臣武);  Zhang K(张坤);  Chen GN(陈光南);  Wu, CW (reprint author), Chinese Acad Sci, Inst Mech, 15 Beisihuanxi Rd, Beijing 100190, Peoples R China.
Adobe PDF(1713Kb)  |  收藏  |  浏览/下载：856/183  |  提交时间：2009/08/03
Hard Coating  Ductile Substrate  Periodic Surface Hardened Regions  Cyclic Bending  Interface Fracture  Subsurface Inclusions  Segmentation Cracks  Steel Substrate  Indentation  Stresses  Fracture  Design  
On The Interaction Of Channeling/Segmentation Cracks Of Coating: Study On The Critical Spacing 期刊论文
Engineering Fracture Mechanics, 2008, 页码: 2531-2541
作者:  Wu CW(吴臣武);  Chen GN(陈光南);  Zhang K(张坤);  Liang NG(梁乃刚);  Wu, CW (reprint author), Chinese Acad Sci, Inst Mech, Ctr Mat Proc, 15 Beisihuanxi Rd, Beijing 100080, Peoples R China.
Adobe PDF(847Kb)  |  收藏  |  浏览/下载：828/174  |  提交时间：2009/08/03
Coating  Channeling/segmentation Cracks  Critical Spacing  Stress Transfer Length  Thermal Barrier Coatings  Finite-element-method  Thin-films  Stresses  Fracture  
On The Thermally Induced Interfacial Delamination Of A Segmented Coating 期刊论文
Surface & Coatings Technology, 2008, 页码: 2878-2884
作者:  Chen XJ(陈学军);  Chen GN(陈光南);  Zhang K(张坤);  Luo GX(罗耕星);  Xiao JH(肖京华);  Chen, XJ (reprint author), Univ Sci & Technol Beijing, Sch Appl Sci, 30 Xueyuan Rd, Beijing 100083, Peoples R China.
Adobe PDF(1200Kb)  |  收藏  |  浏览/下载：946/204  |  提交时间：2009/08/03
Interfacial Delamination  Thermal Loading  Segmentation Crack  Dimensional Analysis  Finite Element Method  Barrier Coatings  Cracks  Fracture  System  Films  
A special method to evaluate the strong adhesion between brittle coating and ductile substrate 会议论文
Asian Pacific Conference for Fracture and Strength (APCFS, Sanya, PEOPLES R CHINA, NOV 22-25, 2006
作者:  Zhang K(张坤);  Peng Q(彭青);  Chen GN(陈光南);  Zhang K
浏览  |  Adobe PDF(879Kb)  |  收藏  |  浏览/下载：620/113  |  提交时间：2009/07/23
Cross-sectional Indentation  Interfacial Adhesion  Evaluation  Cross-sectional Nanoindentation  Thin-film  
Degradation failure features of chromium-plated gun barrels with a laser-discrete-quenched substrate 期刊论文
Surface & Coatings Technology, 2007, 卷号: 201, 期号: 24, 页码: 9558-9564
作者:  Li HX(李怀学);  Chen GN(陈光南);  Zhang K(张坤);  Luo GX(罗耕星);  Ye ZJ(叶智军);  Li, HX (reprint author), Chinese Acad Sci, Inst Mech, Beijing 100080, Peoples R China.
Adobe PDF(3207Kb)  |  收藏  |  浏览/下载：778/193  |  提交时间：2009/08/03
Gun Bore  Electrodeposited Chromium  Interface  Laser-discrete Quenching  Bore Erosion  Thermal-damage  Army Cannons  Coatings  System  Mechanisms  Stresses  Cracking  
The Effect of Periodic Segmentation Cracks on the Interfacial Debonding: Study on Interfacial Stresses 期刊论文
Surface & Coatings Technology, 2006, 卷号: 201, 期号: 1-2, 页码: 287-291
作者:  Wu CW(吴臣武);  Chen GN(陈光南);  Zhang K(张坤);  Luo GX(罗耕星);  Liang NG(梁乃刚);  Wu, C (reprint author), Chinese Acad Sci, Inst Mech, Surface Modificat Lab, Beijing 100080, Peoples R China.
Adobe PDF(249Kb)  |  收藏  |  浏览/下载：626/209  |  提交时间：2007/06/15
Characteristics of the interface of a laser-quenched steel substrate and chromium electroplate 期刊论文
Surface & Coatings Technology, 2006, 卷号: 201, 期号: 3-4, 页码: 902-907
作者:  Li HX(李怀学);  Chen GN(陈光南);  Zhang GX(张国祥);  Zhang K(张坤);  Luo GX(罗耕星);  Li, HX (reprint author), Chinese Acad Sci, Inst Mech, Surface Modificat Lab, Beijing 100080, Peoples R China.
Adobe PDF(467Kb)  |  收藏  |  浏览/下载：683/204  |  提交时间：2009/08/03
Interfaces  Electroplating  Chromium  Laser Quenching  Coatings  Erosion