On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder 期刊论文
Surface & Coatings Technology, 2009, 卷号: 203, 期号: 9, 页码: 1114-1120
作者:  Chen XJ(陈学军);  Chen GN(陈光南);  Chen XJ
Adobe PDF(1070Kb)  |  收藏  |  浏览/下载：1042/150  |  提交时间：2009/08/03
Segmented Coating  Cracking  Thermal Stress Intensity Factor (Tsif)  Finite Element Method  Thick-walled Cylinder  Barrier Coatings  Axial Cracks  Shock  Fracture  Delamination  Stability  
Interface Fracture Behavior Of Electroplated Coating On Metal Substrate Under Compressive Strain 期刊论文
Journal of Materials Processing Technology, 2009, 卷号: 209, 期号: 3, 页码: 1337-1341
作者:  Zhang K(张凯);  Zhang K(张坤);  Li HX(李怀学);  Chen GN(陈光南);  Zhang K
Adobe PDF(619Kb)  |  收藏  |  浏览/下载：1061/167  |  提交时间：2009/08/03
Electroplated Coating  Interface Fracture  Compressive Strain  T-bend Test  
On The Cyclic Bending Behaviour Of A Hard Coating On A Ductile Substrate With Periodic Surface Hardened Regions 期刊论文
International Journal of Solids and Structures, 2008, 页码: 5661-5674
作者:  Wu CW(吴臣武);  Zhang K(张坤);  Chen GN(陈光南);  Wu, CW (reprint author), Chinese Acad Sci, Inst Mech, 15 Beisihuanxi Rd, Beijing 100190, Peoples R China.
Adobe PDF(1713Kb)  |  收藏  |  浏览/下载：856/183  |  提交时间：2009/08/03
Hard Coating  Ductile Substrate  Periodic Surface Hardened Regions  Cyclic Bending  Interface Fracture  Subsurface Inclusions  Segmentation Cracks  Steel Substrate  Indentation  Stresses  Fracture  Design  
Measurement Of Fracture Toughness And Interfacial Shear Strength Of Hard And Brittle Cr Coating On Ductile Steel Substrate 期刊论文
Surface Engineering, 2008, 页码: 332-336
作者:  Yang BQ(杨班权);  Zhang K(张坤);  Chen GN(陈光南);  Luo GX(罗耕星);  Xiao JH(肖京华);  Yang, BQ (reprint author), Armored Force Engn Inst, Dept Mech Engn, Div Engn Mech, 21 Jia Kan, Beijing 100072, Peoples R China.
Adobe PDF(309Kb)  |  收藏  |  浏览/下载：926/219  |  提交时间：2009/08/03
Hard And Brittle Coating  Fracture Toughness  Ductile Steel Substrate  Interfacial Shear Strength  Tensile Test  Thermal Barrier Coatings  Thin-films  Adhesion  Cracking  Decohesion  Behavior  Indentation  Chromium  Erosion  Tensile  
On The Interaction Of Channeling/Segmentation Cracks Of Coating: Study On The Critical Spacing 期刊论文
Engineering Fracture Mechanics, 2008, 页码: 2531-2541
作者:  Wu CW(吴臣武);  Chen GN(陈光南);  Zhang K(张坤);  Liang NG(梁乃刚);  Wu, CW (reprint author), Chinese Acad Sci, Inst Mech, Ctr Mat Proc, 15 Beisihuanxi Rd, Beijing 100080, Peoples R China.
Adobe PDF(847Kb)  |  收藏  |  浏览/下载：828/174  |  提交时间：2009/08/03
Coating  Channeling/segmentation Cracks  Critical Spacing  Stress Transfer Length  Thermal Barrier Coatings  Finite-element-method  Thin-films  Stresses  Fracture  
On The Thermally Induced Interfacial Delamination Of A Segmented Coating 期刊论文
Surface & Coatings Technology, 2008, 页码: 2878-2884
作者:  Chen XJ(陈学军);  Chen GN(陈光南);  Zhang K(张坤);  Luo GX(罗耕星);  Xiao JH(肖京华);  Chen, XJ (reprint author), Univ Sci & Technol Beijing, Sch Appl Sci, 30 Xueyuan Rd, Beijing 100083, Peoples R China.
Adobe PDF(1200Kb)  |  收藏  |  浏览/下载：946/204  |  提交时间：2009/08/03
Interfacial Delamination  Thermal Loading  Segmentation Crack  Dimensional Analysis  Finite Element Method  Barrier Coatings  Cracks  Fracture  System  Films  
Effect of a laser pre-quenched steel substrate surface on the crack driving force in a coating-steel substrate system 期刊论文
Acta Materialia, 2007, 卷号: 55, 期号: 13, 页码: 4349-4358
作者:  Yang BQ(杨班权);  Zhang K(张凯);  Chen GN(陈光南);  Luo GX(罗耕星);  Xiao JH(肖京华);  Yang, BQ (reprint author), Armored Forces Engn Inst, Dept Mech Engn, Div Engn Mech, 21 Du Jia Kan, Beijing 100072, Peoples R China.
Adobe PDF(564Kb)  |  收藏  |  浏览/下载：887/277  |  提交时间：2009/08/03
Laser Pre-quenching  Crack Driving Force  Residual Compressive Stress  Hardness Gradient Effect  Coating/pre-quenched Steel Substrate System  Thermal Barrier Coatings  Thin-films  Conical Indentation  Plastic Solids  Interface  Fatigue  Fracture  Carbon  Behavior  Growth