喷丸对激光辅助成形铝合金样件拉-拉疲劳性能的影响

IMECH-IR > 先进制造工艺力学实验室

	喷丸对激光辅助成形铝合金样件拉-拉疲劳性能的影响
其他题名	Influence of Shot Peening on Tension-Tension Fatigue Property of Laser Aided Forming Aluminum Alloy Samples
	王明星; 陈光南; 彭青
发表期刊	航空学报
	2011
卷号	32 期号:7 页码:1351-1356
ISSN	1000-6893
摘要	为了研究激光辅助成形样件的疲劳性能及喷丸处理的作用规律,以2024铝合金板材为对象,对原始、激光辅助成形以及激光辅助成形后再喷丸等样件的微观组织、显微硬度、残余应力和拉-拉疲劳性能进行了对比分析研究。结果表明:激光辅助成形后,样件的组织和微结构未发现明显变化,但其硬度和残余拉应力水平有所下降;喷丸处理的激光辅助成形样件表层组织改变、显微硬度提高、其拉-拉疲劳寿命显著提高,不仅高于激光辅助成形样件,也高于初始样件。
其他摘要	With the 2024 aluminum alloy plate as the main object,microstructures,microhardness,residual stresses and tension-tension fatigue properties of as-machined aluminum samples,laser aided forming samples and shot peening samples were studied.The results show that microstructures of laser aided forming sample were not varied obvious,but microhardness and extensive residual stress decreased;and surface microstructures were varied and microhardness was raised in shot peening samples.Shot peening can greatly improve fatigue properties.Tension-tension fatigue lives of shot peening samples were not only higher than laser aided forming samples,but higher than as-machined aluminum samples. Key words
关键词	铝合金疲劳激光喷丸微观组织残余应力
学科领域	力学
URL	查看原文
收录类别	EI ; CSCD
语种	中文
项目资助者	国家自然科学基金(50901084,10872199);中国博士后科学基金(20090460537)~~
CSCD记录号	CSCD:4277696
课题组名称	MAM表面与界面改性
引用统计	被引频次：3[CSCD] [CSCD记录]
文献类型	期刊论文
条目标识符	http://dspace.imech.ac.cn/handle/311007/45155
专题	先进制造工艺力学实验室
通讯作者	王明星
推荐引用方式 GB/T 7714	王明星,陈光南,彭青. 喷丸对激光辅助成形铝合金样件拉-拉疲劳性能的影响[J]. 航空学报,2011,32,7,:1351-1356.
APA	王明星,陈光南,&彭青.(2011).喷丸对激光辅助成形铝合金样件拉-拉疲劳性能的影响.航空学报,32(7),1351-1356.
MLA	王明星,et al."喷丸对激光辅助成形铝合金样件拉-拉疲劳性能的影响".航空学报 32.7(2011):1351-1356.

条目包含的文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
C2011J119.pdf（535KB）			开放获取	--	浏览请求全文