Effects of inclusion size and location on very-high-cycle fatigue behavior for high strength steels | |
Lei ZQ(雷铮强); Hong YS(洪友士); Xie JJ(谢季佳); Sun CQ(孙成奇); Zhao AG(赵爱国); hongys@imech.ac.cn | |
发表期刊 | MATERIALS SCIENCE AND ENGINEERING A |
2012-12-15 | |
卷号 | 558页码:234-241 |
ISSN | 0921-5093 |
摘要 | Fatigue tests with rotary bending (52.5 Hz) and ultrasonic cycling (20 kHz) methods were performed, respectively on two high strength steels so as to investigate the effects of inclusion size and location on the fatigue behavior from low cycle fatigue to very-high-cycle fatigue (VHCF) regimes. Under rotary bending test, four fracture patterns were observed with respect to different locations of inclusion on fracture surface. The mean crack growth rate within FGA (fine granular area of crack origin) was estimated to give the value with the magnitude of 10(-13) m/cycle for the specimens with the fracture pattern of "FGA+surface fisheye". Under ultrasonic cycling test, the size effect of inclusions on VHCF was investigated with two groups of specimens. One is with the inclusion size between 20 and 60 mu m and the other is with the inclusion size between 10 and 30 mu m. The results show that large inclusions lowered the proportion of net FGA at given stress levels and led to the shortening of VHCF life. The degradation of VHCF strength caused by the increase of inclusion size is ascribed to the decrease of the critical stress of FGA formation for large inclusions. |
关键词 | Very-high-cycle Fatigue Fga Inclusion High Strength Steels |
学科领域 | 疲劳与断裂力学 |
URL | 查看原文 |
收录类别 | SCI ; EI |
语种 | 英语 |
WOS记录号 | WOS:000311249800033 |
项目资助者 | NSFC[11021262,11172304];National Basic Research Program of China [2012CB937500] |
课题组名称 | LNM金属材料微结构与力学性能 |
论文分区 | 一类 |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://dspace.imech.ac.cn/handle/311007/45846 |
专题 | 非线性力学国家重点实验室 |
通讯作者 | hongys@imech.ac.cn |
推荐引用方式 GB/T 7714 | Lei ZQ,Hong YS,Xie JJ,et al. Effects of inclusion size and location on very-high-cycle fatigue behavior for high strength steels[J]. MATERIALS SCIENCE AND ENGINEERING A,2012,558:234-241. |
APA | Lei ZQ,Hong YS,Xie JJ,Sun CQ,Zhao AG,&hongys@imech.ac.cn.(2012).Effects of inclusion size and location on very-high-cycle fatigue behavior for high strength steels.MATERIALS SCIENCE AND ENGINEERING A,558,234-241. |
MLA | Lei ZQ,et al."Effects of inclusion size and location on very-high-cycle fatigue behavior for high strength steels".MATERIALS SCIENCE AND ENGINEERING A 558(2012):234-241. |
条目包含的文件 | 下载所有文件 | |||||
文件名称/大小 | 文献类型 | 版本类型 | 开放类型 | 使用许可 | ||
SCI-J2012-064.pdf(1782KB) | 开放获取 | 使用许可 | 浏览 下载 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论