The behavior of crack initiation and early growth in high-cycle and very-high-cycle fatigue regimes for a titanium alloy | |
Pan XN(潘向南)![]() ![]() ![]() | |
Source Publication | INTERNATIONAL JOURNAL OF FATIGUE
![]() |
2018-10-01 | |
Volume | 115Issue:SIPages:67-78 |
ISSN | 0142-1123 |
Abstract | The behavior of crack initiation and early growth in high-cycle fatigue (HCF) and very-high-cycle fatigue (VHCF) regimes for a TC4 titanium alloy with equiaxed microstructure was investigated. Fatigue tests were conducted via ultrasonic axial cycling (20 kHz) superimposed by an amount of tensile load. The effect of tensile mean stress on fatigue endurance was plotted with a Haigh diagram formulated by Goodman, Gerber and the present formula. Fractography was observed by scanning electron microscopy, and three failure types of crack initiation were classified: surface-without-RA (rough area), surface-with-RA and interior-with-RA. Profile samples from the crack initiation region were prepared and examined by transmission electron microscopy with selected area electron diffraction. The observations show that a nanograin layer prevails underneath the fracture surface in the RA region only for the VHCF case with a stress ratio R = -1. The nanograin formation mechanism was explained by the numerous cyclic pressing (NCP) model. |
Keyword | Very-high-cycle fatigue Crack initiation Mean stress Titanium alloy Equiaxed microstructure |
DOI | 10.1016/j.ijfatigue.2018.03.021 |
URL | 查看原文 |
Indexed By | SCI ; EI |
Language | 英语 |
WOS ID | WOS:000449895700009 |
WOS Keyword | POISSON DEFECT STATISTICS ; COMPETING FAILURE MODES ; HIGH-STRENGTH STEELS ; TI-6AL-4V ALLOY ; STRESS RATIO ; GIGACYCLE FATIGUE ; ARTIFICIAL DEFECTS ; METALLIC MATERIALS ; FGA FORMATION ; MEAN STRESS |
WOS Research Area | Engineering, Mechanical ; Materials Science, Multidisciplinary |
WOS Subject | Engineering ; Materials Science |
Funding Organization | National Natural Science Foundation of China [11572325] ; Strategic Priority Research Program of the Chinese Academy of Sciences [XDB22040503, XDB22020201] |
Classification | 一类 |
Ranking | 1 |
Citation statistics | |
Document Type | 期刊论文 |
Identifier | http://dspace.imech.ac.cn/handle/311007/78139 |
Collection | 非线性力学国家重点实验室 |
Affiliation | 1.Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China 2.Univ Chinese Acad Sci, Sch Engn Sci, Beijing 100049, Peoples R China |
Recommended Citation GB/T 7714 | Pan XN,Su H,Sun CQ,et al. The behavior of crack initiation and early growth in high-cycle and very-high-cycle fatigue regimes for a titanium alloy[J]. INTERNATIONAL JOURNAL OF FATIGUE,2018,115(SI):67-78. |
APA | Pan XN,Su H,Sun CQ,&Hong YS.(2018).The behavior of crack initiation and early growth in high-cycle and very-high-cycle fatigue regimes for a titanium alloy.INTERNATIONAL JOURNAL OF FATIGUE,115(SI),67-78. |
MLA | Pan XN,et al."The behavior of crack initiation and early growth in high-cycle and very-high-cycle fatigue regimes for a titanium alloy".INTERNATIONAL JOURNAL OF FATIGUE 115.SI(2018):67-78. |
Files in This Item: | Download All | |||||
File Name/Size | DocType | Version | Access | License | ||
IrJ2018361.pdf(6409KB) | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | View Download |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment