Experimental study on the impact resistance and damage tolerance of thermoplastic FMLs | |
Yang, Lei; Liao, Zhenhao; Qiu C(邱诚); Hong, Zijing; Yang, Jinglei | |
通讯作者 | Yang, Lei(yanglei@szu.edu.cn) |
发表期刊 | THIN-WALLED STRUCTURES |
2024-03-01 | |
卷号 | 196页码:11 |
ISSN | 0263-8231 |
摘要 | This study aimed to enhance the impact resistance of fiber metal laminates (FMLs) and achieve lightweight optimization by incorporating a new thermoplastic resin, a titanium alloy and ultra-high-molecular-weight polyethylene (UHMWPE) fiber to produce a novel type of FMLs (PEFMLs). The impact resistance of PEFMLs was analyzed through low-velocity impact tests conducted at different energy levels. Subsequently, the residual compression-after-impact (CAI) strength of the PEFMLs was evaluated through compression tests on the impacted specimens. The experimental findings revealed that PEFMLs exhibited subcritical failure when subjected to impact energies less than 35 J, with a penetration energy threshold of 55 J. Higher impact energies resulted in larger damage areas and increased plate buckling of PEFMLs, consequently leading to reduced CAI strength. The presence of metal, thermoplastic resin and UHMWPE in the PEFMLs effectively dissipated a substantial amount of impact energy while maintaining their structural integrity during both the impact and compression processes. |
关键词 | Thermoplastic resin FMLs Impact behaviour Compression after impact |
DOI | 10.1016/j.tws.2023.111435 |
收录类别 | SCI ; EI |
语种 | 英语 |
WOS记录号 | WOS:001140001700001 |
关键词[WOS] | LOW-VELOCITY IMPACT ; COMPOSITES ; BEHAVIOR ; FAILURE ; ENERGY ; TEMPERATURE ; MATRIX |
WOS研究方向 | Engineering ; Mechanics |
WOS类目 | Engineering, Civil ; Engineering, Mechanical ; Mechanics |
资助项目 | Natural Science Foundation of Shenzhen City[20200814105851001] |
项目资助者 | Natural Science Foundation of Shenzhen City |
论文分区 | 一类 |
力学所作者排名 | 3 |
RpAuthor | Yang, Lei |
引用统计 | |
文献类型 | 期刊论文 |
条目标识符 | http://dspace.imech.ac.cn/handle/311007/94071 |
专题 | 流固耦合系统力学重点实验室 |
推荐引用方式 GB/T 7714 | Yang, Lei,Liao, Zhenhao,Qiu C,et al. Experimental study on the impact resistance and damage tolerance of thermoplastic FMLs[J]. THIN-WALLED STRUCTURES,2024,196:11. |
APA | Yang, Lei,Liao, Zhenhao,邱诚,Hong, Zijing,&Yang, Jinglei.(2024).Experimental study on the impact resistance and damage tolerance of thermoplastic FMLs.THIN-WALLED STRUCTURES,196,11. |
MLA | Yang, Lei,et al."Experimental study on the impact resistance and damage tolerance of thermoplastic FMLs".THIN-WALLED STRUCTURES 196(2024):11. |
条目包含的文件 | 条目无相关文件。 |
除非特别说明,本系统中所有内容都受版权保护,并保留所有权利。
修改评论