Research on fracture behavior of a Cr coating/ laser pre-quenched steel substrate system under thermal fatigue loading 会议论文
International Conference on Vehicle and Mechanical Engineering and Information Technology, VMEIT 2014, Beijing, China, February 19, 2014 - February 20, 2014
Authors:  Yang BQ(杨班权);  Chen GN(陈光南);  Chen XJ;  Sun WH;  Chen HQ;  Pan JW;  Chen Y
View  |  Adobe PDF(340Kb)  |  Favorite  |  View/Download：356/117  |  Submit date：2017/05/27
Cr Coating/laser Pre-quenched Steel Substrate Systems  Cr Coatings  Crack Density  Failure Process  Fracture Behavior  Steel Substrate  Substrate Surface  Thermal Fatigue Loadings  
Research on interfacial cracking of a Cr coating/steel substrate with and without laser pre-quenching treatment under thermal fatigue loading 会议论文
3rd International Conference on Digital Manufacturing and Automation, ICDMA 2012, Guangxi, China, AUG 01-02, 2012
Authors:  Yang BQ(杨班权);  Chen GN(陈光南);  Chen XJ(陈学军);  Sun WH;  Chen HQ;  Pan JW;  Chen Y;  Yang BQ(杨班权)
View  |  Adobe PDF(329Kb)  |  Favorite  |  View/Download：1077/207  |  Submit date：2013/02/26
Chromate Coatings  Chromium  Manufacture  Quenching  Substrates  Thermal Fatigue  Interfacial Adhesions  Interfacial Cracking  Loading Condition  Steel Substrate  Substrate Surface  
Research on the micro-crack density of a chromium coating/steel substrate with and without laser pre-quenching treatment 会议论文
2011 1st International Conference on High Performance Structures and Materials Engineering, ICHPSM 2011, Beijing, China, MAY 05-06, 2011
Authors:  Yang BQ(杨班权);  Chen GN(陈光南);  Chen XJ(陈学军);  Yang BQ(杨班权)
Adobe PDF(368Kb)  |  Favorite  |  View/Download：851/163  |  Submit date：2013/02/26
Chromate Coatings  Chromium  Cracks  Density (Specific Gravity)  Mechanical Properties  Quenching  Chromium Coatings  Crack Density  Material Systems  Micro-crack Density  Quenched Steel  Quenched Substrates  Quenching Treatment  Steel Substrate  Substrate Surface  Work Pieces  
Measurement Of Fracture Toughness And Interfacial Shear Strength Of Hard And Brittle Cr Coating On Ductile Steel Substrate 期刊论文
Surface Engineering, 2008, 页码: 332-336
Authors:  Yang BQ(杨班权);  Zhang K(张坤);  Chen GN(陈光南);  Luo GX(罗耕星);  Xiao JH(肖京华);  Yang, BQ (reprint author), Armored Force Engn Inst, Dept Mech Engn, Div Engn Mech, 21 Jia Kan, Beijing 100072, Peoples R China.
Adobe PDF(309Kb)  |  Favorite  |  View/Download：950/239  |  Submit date：2009/08/03
Hard And Brittle Coating  Fracture Toughness  Ductile Steel Substrate  Interfacial Shear Strength  Tensile Test  Thermal Barrier Coatings  Thin-films  Adhesion  Cracking  Decohesion  Behavior  Indentation  Chromium  Erosion  Tensile  
On the tensile behaviors of a hard chromium coating plated on a steel substrate with periodic subsurface inclusions 期刊论文
Surface & Coatings Technology, 2007, 卷号: 201, 期号: 18, 页码: 7699-7705
Authors:  Wu CW(吴臣武);  Yang BQ(杨班权);  Chen GN(陈光南);  Zhang K(张坤);  Xiao JH(肖京华);  Wu, CW (reprint author), Chinese Acad Sci, Inst Mech, 15 Beisihuanxi Rd, Beijing 100080, Peoples R China.
Adobe PDF(1366Kb)  |  Favorite  |  View/Download：1211/441  |  Submit date：2009/10/22
Coating  Periodic Subsurface Inclusions  Tensile Behaviors  Fem  
Degradation failure features of chromium-plated gun barrels with a laser-discrete-quenched substrate 期刊论文
Surface & Coatings Technology, 2007, 卷号: 201, 期号: 24, 页码: 9558-9564
Authors:  Li HX(李怀学);  Chen GN(陈光南);  Zhang K(张坤);  Luo GX(罗耕星);  Ye ZJ(叶智军);  Li, HX (reprint author), Chinese Acad Sci, Inst Mech, Beijing 100080, Peoples R China.
Adobe PDF(3207Kb)  |  Favorite  |  View/Download：814/206  |  Submit date：2009/08/03
Gun Bore  Electrodeposited Chromium  Interface  Laser-discrete Quenching  Bore Erosion  Thermal-damage  Army Cannons  Coatings  System  Mechanisms  Stresses  Cracking  
Characteristics of the interface of a laser-quenched steel substrate and chromium electroplate 期刊论文
Surface & Coatings Technology, 2006, 卷号: 201, 期号: 3-4, 页码: 902-907
Authors:  Li HX(李怀学);  Chen GN(陈光南);  Zhang GX(张国祥);  Zhang K(张坤);  Luo GX(罗耕星);  Li, HX (reprint author), Chinese Acad Sci, Inst Mech, Surface Modificat Lab, Beijing 100080, Peoples R China.
Adobe PDF(467Kb)  |  Favorite  |  View/Download：712/208  |  Submit date：2009/08/03
Interfaces  Electroplating  Chromium  Laser Quenching  Coatings  Erosion  
Characterization of a Laser-Discrete Quenched Steel Substrate/Chromium System by Dissolving Coatings 期刊论文
Surface & Coatings Technology, 2006, 卷号: 201, 期号: 6, 页码: 3709-3714
Authors:  Li HX(李怀学);  Zhang K(张坤);  Chen GN(陈光南);  Luo GX(罗耕星);  Ye ZJ(叶智军);  Li, HX (reprint author), Chinese Acad Sci, Inst Mech, Surface Modificat Lab, Beijing 100080, Peoples R China.
Adobe PDF(1885Kb)  |  Favorite  |  View/Download：705/146  |  Submit date：2007/06/15
On the Formation of Periodic Segmentation Cracks in a Coating Plated on a Substrate with Periodic Subsurface Inclusions 期刊论文
Surface & Coatings Technology, 2006, 卷号: 201, 期号: 6, 页码: 2364-2368
Authors:  Wu CW(吴臣武);  Chen GN(陈光南);  Zhang K(张坤);  Hu Y(胡莹);  Liang NG(梁乃刚);  Zhang, K (reprint author), Chinese Acad Sci, Inst Mech, Ctr Mat Proc, 15 Beisihuanxi Rd, Beijing 100080, Peoples R China.
Adobe PDF(599Kb)  |  Favorite  |  View/Download：720/165  |  Submit date：2007/06/15