Uniaxial tensile and cross-sectional indentation tests to investigate the adhesion between the brittle Cr coating and the ductile steel substrate 会议论文
2011 1st International Conference on Mechanical Engineering, ICME 2011, Phuket, Thailand, APR 03-04, 2011
作者:  Yang BQ(杨班权);  Chen GN(陈光南);  Chen XJ(陈学军);  Yang BQ(杨班权)
Adobe PDF(246Kb)  |  收藏  |  浏览/下载：772/113  |  提交时间：2013/02/26
Adhesion  Carbon Steel  Mechanical Engineering  Shear Flow  Shear Strength  Substrates  Tensile Strength  Tensile Testing  Testing  Coating-substrate Systems  Cr Coating  Cross-sectional Indentations  Crucial Parameters  Ductile Steel Substrate  Flow Stress  Interfacial Decohesion  Lower Bounds  Maximum Shears  Normal Medium Carbon Steel  Ultimate Shear Strength  Uniaxial Tensile Test  
On The Thermally Induced Cracking Of A Segmented Coating Deposited On The Outer Surface Of A Hollow Cylinder 期刊论文
Surface & Coatings Technology, 2009, 卷号: 203, 期号: 9, 页码: 1114-1120
作者:  Chen XJ(陈学军);  Chen GN(陈光南);  Chen XJ
Adobe PDF(1070Kb)  |  收藏  |  浏览/下载：1049/153  |  提交时间：2009/08/03
Segmented Coating  Cracking  Thermal Stress Intensity Factor (Tsif)  Finite Element Method  Thick-walled Cylinder  Barrier Coatings  Axial Cracks  Shock  Fracture  Delamination  Stability  
On The Cyclic Bending Behaviour Of A Hard Coating On A Ductile Substrate With Periodic Surface Hardened Regions 期刊论文
International Journal of Solids and Structures, 2008, 页码: 5661-5674
作者:  Wu CW(吴臣武);  Zhang K(张坤);  Chen GN(陈光南);  Wu, CW (reprint author), Chinese Acad Sci, Inst Mech, 15 Beisihuanxi Rd, Beijing 100190, Peoples R China.
Adobe PDF(1713Kb)  |  收藏  |  浏览/下载：860/184  |  提交时间：2009/08/03
Hard Coating  Ductile Substrate  Periodic Surface Hardened Regions  Cyclic Bending  Interface Fracture  Subsurface Inclusions  Segmentation Cracks  Steel Substrate  Indentation  Stresses  Fracture  Design  
Measurement Of Fracture Toughness And Interfacial Shear Strength Of Hard And Brittle Cr Coating On Ductile Steel Substrate 期刊论文
Surface Engineering, 2008, 页码: 332-336
作者:  Yang BQ(杨班权);  Zhang K(张坤);  Chen GN(陈光南);  Luo GX(罗耕星);  Xiao JH(肖京华);  Yang, BQ (reprint author), Armored Force Engn Inst, Dept Mech Engn, Div Engn Mech, 21 Jia Kan, Beijing 100072, Peoples R China.
Adobe PDF(309Kb)  |  收藏  |  浏览/下载：929/222  |  提交时间：2009/08/03
Hard And Brittle Coating  Fracture Toughness  Ductile Steel Substrate  Interfacial Shear Strength  Tensile Test  Thermal Barrier Coatings  Thin-films  Adhesion  Cracking  Decohesion  Behavior  Indentation  Chromium  Erosion  Tensile  
On The Interaction Of Channeling/Segmentation Cracks Of Coating: Study On The Critical Spacing 期刊论文
Engineering Fracture Mechanics, 2008, 页码: 2531-2541
作者:  Wu CW(吴臣武);  Chen GN(陈光南);  Zhang K(张坤);  Liang NG(梁乃刚);  Wu, CW (reprint author), Chinese Acad Sci, Inst Mech, Ctr Mat Proc, 15 Beisihuanxi Rd, Beijing 100080, Peoples R China.
Adobe PDF(847Kb)  |  收藏  |  浏览/下载：831/175  |  提交时间：2009/08/03
Coating  Channeling/segmentation Cracks  Critical Spacing  Stress Transfer Length  Thermal Barrier Coatings  Finite-element-method  Thin-films  Stresses  Fracture  
On The Thermally Induced Interfacial Delamination Of A Segmented Coating 期刊论文
Surface & Coatings Technology, 2008, 页码: 2878-2884
作者:  Chen XJ(陈学军);  Chen GN(陈光南);  Zhang K(张坤);  Luo GX(罗耕星);  Xiao JH(肖京华);  Chen, XJ (reprint author), Univ Sci & Technol Beijing, Sch Appl Sci, 30 Xueyuan Rd, Beijing 100083, Peoples R China.
Adobe PDF(1200Kb)  |  收藏  |  浏览/下载：953/207  |  提交时间：2009/08/03
Interfacial Delamination  Thermal Loading  Segmentation Crack  Dimensional Analysis  Finite Element Method  Barrier Coatings  Cracks  Fracture  System  Films  
Effect of a laser pre-quenched steel substrate surface on the crack driving force in a coating-steel substrate system 期刊论文
Acta Materialia, 2007, 卷号: 55, 期号: 13, 页码: 4349-4358
作者:  Yang BQ(杨班权);  Zhang K(张凯);  Chen GN(陈光南);  Luo GX(罗耕星);  Xiao JH(肖京华);  Yang, BQ (reprint author), Armored Forces Engn Inst, Dept Mech Engn, Div Engn Mech, 21 Du Jia Kan, Beijing 100072, Peoples R China.
Adobe PDF(564Kb)  |  收藏  |  浏览/下载：891/279  |  提交时间：2009/08/03
Laser Pre-quenching  Crack Driving Force  Residual Compressive Stress  Hardness Gradient Effect  Coating/pre-quenched Steel Substrate System  Thermal Barrier Coatings  Thin-films  Conical Indentation  Plastic Solids  Interface  Fatigue  Fracture  Carbon  Behavior  Growth  
Degradation failure features of chromium-plated gun barrels with a laser-discrete-quenched substrate 期刊论文
Surface & Coatings Technology, 2007, 卷号: 201, 期号: 24, 页码: 9558-9564
作者:  Li HX(李怀学);  Chen GN(陈光南);  Zhang K(张坤);  Luo GX(罗耕星);  Ye ZJ(叶智军);  Li, HX (reprint author), Chinese Acad Sci, Inst Mech, Beijing 100080, Peoples R China.
Adobe PDF(3207Kb)  |  收藏  |  浏览/下载：784/195  |  提交时间：2009/08/03
Gun Bore  Electrodeposited Chromium  Interface  Laser-discrete Quenching  Bore Erosion  Thermal-damage  Army Cannons  Coatings  System  Mechanisms  Stresses  Cracking  
The plastic instability behaviour of laser-textured steel sheet 期刊论文
Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, 1996, 卷号: 219, 期号: 1-2, 页码: 156-161
作者:  Shen H;  Chen GN(陈光南);  Li GC(李国琛);  Shen, H (reprint author), ACAD SINICA,INST MECH,BEIJING 100080,PEOPLES R CHINA.
Adobe PDF(797Kb)  |  收藏  |  浏览/下载：512/151  |  提交时间：2009/08/03
Laser-texturing  Instability  Voids  Steel Sheet  Shear