Undercooling and Rapid Solidification of Nb-Si Eutectic Alloys Studied by Long Drop Tube

IMECH-IR > 力学所知识产出(1956-2008)

	Undercooling and Rapid Solidification of Nb-Si Eutectic Alloys Studied by Long Drop Tube
	Wang YR(王育人); Dong SY; Wei BC(魏炳忱); Li WH(李维火)
会议录名称	TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2006,16(suppl.2):S89-S92
	2005-10-09
会议名称	6th International Workshop on Advanced Intermetallic and Metallic Materials, OCT 09-15, 2005, Yangzhou, PEOPLES R CHINA
摘要	Niobium-silicide alloys have great potential for high temperature turbine applications. The two-phase Nb/Nb5Si3 in situ composites exhibit a good balance in mechanical properties. Using the 52 in drop tube, the effect of undercooling and rapid solidification on the solidification process and micro-structural characterization of Nb-Si eutectic alloy was studied. The microstructures of the Nb-Si composites were investigated by optics microscope (OM), X-ray diffraction (XRD) and scanning electron microscope (SEM) equipped with X-ray energy dispersive spectrometry (EDS). Up to 480 K, deep undercooling of the Nb-Si eutectic samples was successfully obtained, which corresponds to 25% of the liquidus temperature. Contrasting to the conventional microstructure usually found in the Nb-Si eutectic alloy, the microstructure of the undercooled sample is divided into the fine and coarse regions. The most commonly observed microstructure is Nb+Nb5Si3, and the Nb3Si phase is not be found. The change of coarseness of microstructure is due to different cooling rates during and after recalescence. The large undercooling is sufficient to completely bypass the high temperature phase field.
WOS记录号	WOS:000241774000019
收录类别	CPCI-S
语种	英语
引用统计	被引频次：1[WOS] [WOS记录] [WOS相关记录]
文献类型	会议论文
条目标识符	http://dspace.imech.ac.cn/handle/311007/13763
专题	力学所知识产出(1956-2008)
通讯作者	Wang YR(王育人)
推荐引用方式 GB/T 7714	Wang YR,Dong SY,Wei BC,et al. Undercooling and Rapid Solidification of Nb-Si Eutectic Alloys Studied by Long Drop Tube[C]TRANSACTIONS OF NONFERROUS METALS SOCIETY OF CHINA,2006,16(suppl.2):S89-S92,2005.

条目包含的文件		下载所有文件
文件名称/大小	文献类型	版本类型	开放类型	使用许可
06z219.pdf（464KB）			开放获取	--	浏览下载