| Observation of ceramic cracking during quenching |
| Shao YF(邵颖峰); Song F(宋凡); Liu BY; Li W; Li L(李龙); Jiang CP; Shao, YF (reprint author), Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing, Peoples R China.
|
发表期刊 | JOURNAL OF THE AMERICAN CERAMIC SOCIETY
|
| 2017-02-01
|
卷号 | 100期号:2页码:520-523 |
ISSN | 0002-7820
|
摘要 | It is difficult to observe the thermal shock cracking in real time so the measurement of the crack after thermal shock is considered as an alternative method. This paper proposes a new experimental method which can exhibit the thermal shock cracking in real time by water quenching of translucent ceramic and high-speed imaging. The crack propagation is captured and the crack growth rate is calculated. The results confirm the previous theoretical predictions of crack propagation under thermal shock. This paper expands the research on understanding the failure mechanisms of ceramic materials in thermal shock. |
关键词 | Alumina
Cracks/cracking
Thermal Shock/Thermal Shock Resistance
|
DOI | 10.1111/jace.14674
|
收录类别 | SCI
; EI
|
语种 | 英语
|
WOS记录号 | WOS:000394545900009
|
关键词[WOS] | THERMAL-SHOCK
; NUMERICAL SIMULATIONS
; BRITTLE MATERIALS
; PROPAGATION
; INITIATION
; PATTERNS
|
WOS研究方向 | Materials Science
|
WOS类目 | Materials Science, Ceramics
|
项目资助者 | National Natural Science Foundations of China(11102208
; 11572326
; 11232013
; 11472285)
|
课题组名称 | LNM生物材料微结构和力学性能
|
论文分区 | 一类
|
力学所作者排名 | 1
|
引用统计 |
|
文献类型 | 期刊论文
|
条目标识符 | http://dspace.imech.ac.cn/handle/311007/60578
|
专题 | 非线性力学国家重点实验室
|
通讯作者 | Shao, YF (reprint author), Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing, Peoples R China. |
推荐引用方式 GB/T 7714 |
Shao YF,Song F,Liu BY,et al. Observation of ceramic cracking during quenching[J]. JOURNAL OF THE AMERICAN CERAMIC SOCIETY,2017,100,2,:520-523.
|
APA |
邵颖峰.,宋凡.,Liu BY.,Li W.,李龙.,...&Shao, YF .(2017).Observation of ceramic cracking during quenching.JOURNAL OF THE AMERICAN CERAMIC SOCIETY,100(2),520-523.
|
MLA |
邵颖峰,et al."Observation of ceramic cracking during quenching".JOURNAL OF THE AMERICAN CERAMIC SOCIETY 100.2(2017):520-523.
|
修改评论