| Fatigue Growth Behaviour of Two Interacting Cracks with Different Crack Offset | |
| Jin HJ(晋会锦)1; Cui B2; Mao L3 | |
| Corresponding Author | Jin, Huijin(jinhuijin863@163.com) |
| Source Publication | MATERIALS
 |
| 2019-11-01 | |
| Volume | 12Issue:21Pages:9 |
| Abstract | Under cyclic fatigue load, multiple cracks would significantly deteriorate the service life of the components with respect to the case of a single crack owing to the crack interaction. The present study aims to explore the effect of crack interaction on the fatigue growth behaviour of samples with different crack offset. In this study, fatigue crack growth tests were performed for samples containing a single crack and non-collinear cracks of different crack offset in an aluminum-lithium alloy. It was shown that the two facing non-collinear cracks changed their growth direction when the cracks were overlapped, resulting in load mode transfers from mode I to I + II mixed mode. Then, the interaction behaviour was studied by establishing the finite element models to calculate the stress intensity factor K of samples with different crack offset. The results indicated that the K decreased, largely owing to the shielding effect as the two cracks overlapped, leading to retardation of crack growth in the position of overlap, especially for the specimens with a small crack offset. It was also shown that the interaction effect could change from positive to negative during the process of the multiple cracks' growth, thus leading to the acceleration or deceleration of crack growth rates, suggesting that the influence of interaction on cracks' growth behaviour could vary with the different stages of crack growth. |
| Keyword | non-collinear cracks finite element analysis fatigue crack growth interacting behaviour |
| DOI | 10.3390/ma12213526 |
| Indexed By | SCI ; EI |
| Language | 英语 |
| WOS ID | WOS:000502798800067 |
| WOS Keyword | INTENSITY FACTOR CALCULATION ; MULTIPLE CRACKS ; SIMULATION ; FRACTURE ; JOINTS |
| WOS Research Area | Materials Science |
| WOS Subject | Materials Science, Multidisciplinary |
| Funding Project | National Ministry of Industry and Information Technology Project[M J-F-2011-34] |
| Funding Organization | National Ministry of Industry and Information Technology Project |
| Classification | 二类 |
| Ranking | 1 |
| Contributor | Jin, Huijin |
| Citation statistics | |
| Document Type | 期刊论文 |
| Identifier | http://dspace.imech.ac.cn/handle/311007/81249 |
| Collection | 非线性力学国家重点实验室 |
| Affiliation | 1.Chinese Acad Sci, Inst Mech, State Key Lab Nonlinear Mech, Beijing 100190, Peoples R China; 2.Anhui Univ Technol, Sch Mat Sci & Engn, Maanshan 243000, Peoples R China; 3.Beihang Univ, Sch Mat Sci & Engn, Beijing 100191, Peoples R China |
| Recommended Citation GB/T 7714 | Jin HJ,Cui B,Mao L. Fatigue Growth Behaviour of Two Interacting Cracks with Different Crack Offset[J]. MATERIALS,2019,12(21):9. |
| APA | 晋会锦,Cui B,&Mao L.(2019).Fatigue Growth Behaviour of Two Interacting Cracks with Different Crack Offset.MATERIALS,12(21),9. |
| MLA | 晋会锦,et al."Fatigue Growth Behaviour of Two Interacting Cracks with Different Crack Offset".MATERIALS 12.21(2019):9. |
| Files in This Item: | Download All | |||||
| File Name/Size | DocType | Version | Access | License | ||
| Jp2019499.pdf（4352KB） | 期刊论文 | 出版稿 | 开放获取 | CC BY-NC-SA | View Download | |
Items in the repository are protected by copyright, with all rights reserved, unless otherwise indicated.
Edit Comment